Thermodur 2714 Bar

Alternative und Handelsbezeichungen
DIN EN ISO 55NiCrMoV7, 1.2714, AISI L6, AFNOR 55NCDV7
.XLSX
.PDF
Speichern

Beschreibung

1.2714 (55NiCrMoV7) is a tough die steel with high tempering resistance and good through-hardening properties. This grade is usually supplied in annealed condition or quenched and tempered to a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, flat).

Equivalent Materials

Eigenschaften

Abmessung

Diameter d

20.8 - 755 mm

Mechanisch

Hardness, Brinell HB

355 - 410 [-] at 20 °C

as-delivered condition

Hardness, Rockwell C HRC

56 - 58 [-] at 20 °C

after quenching

Tensile strength Rm

1190 - 1385 MPa at 20 °C

Thermisch

Coefficient of thermal expansion α

1.22E-5 1/K at 100 °C

for 20°C to the mentioned temperature

Grafik anzeigen

Thermal conductivity λ

36 W/(m·K) at 23 °C

Grafik anzeigen

Chemische Eigenschaften

Element

Gew. %

Kommentar

Fe

-

Balance

Ni

1.7 %

Cr

1.1 %

Mn

0.75 %

C

0.56 %

Mehr

Technische Eigenschaften

Application areas

Standard steel for forging dies, press dies, auxiliary tools for extrusion, die holders, armoured trim dies, hot shear blades

Heat Treatment

Soft annealing: 650-700°C (Cooling in furnace) - Hardening: 830-870°C, 860-900 (Oil, Air)

Diese Materialdaten wurden von Deutsche Edelstahlwerke Specialty Steel (DEW) zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.