Allgemein
Property | Value |
---|---|
Dichte | 6.5 g/cm³ Show Supplier Material materials with Dichte of 6.5 g/cm³ |
Kornstruktur | Titanium carbide + martensite |
Mechanisch
Property | Value |
---|---|
Biegefestigkeit | 1500 MPa Show Supplier Material materials with Biegefestigkeit of 1500 MPa |
Druckfestigkeit | 3800 MPa Show Supplier Material materials with Druckfestigkeit of 3800 MPa |
Elastizitätsmodul | 292 GPa Show Supplier Material materials with Elastizitätsmodul of 292 GPa |
Härte, Rockwell C | 69 [-] Show Supplier Material materials with Härte, Rockwell C of 69 [-] |
Schubmodule | 117 GPa Show Supplier Material materials with Schubmodule of 117 GPa |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Koeffizient der thermischen Ausdehnung | 100 °C | 9.2e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.2e-06 1/K | for 20°C to the mentioned temperature |
200 °C | 9.1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.1e-06 1/K | for 20°C to the mentioned temperature | |
300 °C | 9.8e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.8e-06 1/K | for 20°C to the mentioned temperature | |
Wärmeleitfähigkeit | 20.5 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 20.5 W/(m·K) |
Elektrisch
Property | Value |
---|---|
spezifischer Widerstand | 7.5e-07 Ω·m Show Supplier Material materials with spezifischer Widerstand of 7.5e-07 Ω·m |
Magnetisch
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | All cold work applications in cutting and forming engineering, e.g. for cutting and blanking tools, bending jaws, extrusion punches, deep-drawing dies, form and hobbing punches, clamping jaws, blanking sleeves, tools for the processing of steel, non-ferrous metals, aluminium, etc., as well as machine elements such as pulleys, rollers and guides exposed to heavy wear. | |
General machinability | In as-delivered condition, this material can be machined by conventional methods. | |
Heat Treatment | Soft annealing: 750°C,10 hr (Cooling in furnace) Hardness: 49 HRC - Stress-relief-annealing: 600-650°C (cooling in Furnace) - Hardening: 980-1100°C and quenching in vacuum (1 bar N2) - Temepering 150°C (Hardness:69 HRC) |