Eigenschaften
Allgemein
| Property | Value |
|---|---|
Dichte | 6.6 g/cm³ Show Supplier Material materials with Dichte of 6.6 g/cm³ |
Kornstruktur | Titanium carbide + nickel martensite |
Mechanisch
| Property | Value |
|---|---|
Biegefestigkeit | 1200 MPa Show Supplier Material materials with Biegefestigkeit of 1200 MPa |
Druckfestigkeit | 2750 MPa Show Supplier Material materials with Druckfestigkeit of 2750 MPa |
Elastizitätsmodul | 294 GPa Show Supplier Material materials with Elastizitätsmodul of 294 GPa |
Härte, Rockwell C | 62 [-] Show Supplier Material materials with Härte, Rockwell C of 62 [-] |
Schubmodule | 117 GPa Show Supplier Material materials with Schubmodule of 117 GPa |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 100 °C | 8.3e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 8.3e-06 1/K | for 20°C to the mentioned temperature |
200 °C | 8.9e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 8.9e-06 1/K | for 20°C to the mentioned temperature | |
300 °C | 9.3e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.3e-06 1/K | for 20°C to the mentioned temperature | |
400 °C | 9.6e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.6e-06 1/K | for 20°C to the mentioned temperature | |
500 °C | 9.9e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.9e-06 1/K | for 20°C to the mentioned temperature | |
600 °C | 1.02e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.02e-05 1/K | for 20°C to the mentioned temperature | |
700 °C | 9.2e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.2e-06 1/K | for 20°C to the mentioned temperature | |
800 °C | 9.5e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.5e-06 1/K | for 20°C to the mentioned temperature | |
Wärmeleitfähigkeit | 100 °C | 17.1 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 17.1 W/(m·K) | |
150 °C | 17.8 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 17.8 W/(m·K) | ||
200 °C | 18.8 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 18.8 W/(m·K) | ||
250 °C | 19.9 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 19.9 W/(m·K) | ||
300 °C | 21.2 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 21.2 W/(m·K) | ||
350 °C | 22.6 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 22.6 W/(m·K) | ||
400 °C | 24.2 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 24.2 W/(m·K) | ||
450 °C | 25.9 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 25.9 W/(m·K) | ||
500 °C | 27.6 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 27.6 W/(m·K) | ||
550 °C | 29.5 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 29.5 W/(m·K) | ||
600 °C | 31.5 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 31.5 W/(m·K) |
Elektrisch
| Property | Temperature | Value |
|---|---|---|
spezifischer Widerstand | 20 °C | 1.1e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.1e-06 Ω·m |
100 °C | 1.12e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.12e-06 Ω·m | |
200 °C | 1.17e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.17e-06 Ω·m | |
300 °C | 1.21e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.21e-06 Ω·m | |
400 °C | 1.25e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.25e-06 Ω·m | |
500 °C | 1.31e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.31e-06 Ω·m | |
600 °C | 1.67e-06 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.67e-06 Ω·m |
Magnetisch
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Andere | 30 % Show Supplier Material materials with Andere of 30 % | TiC | |
Chrom | 13.5 % Show Supplier Material materials with Chrom of 13.5 % | ||
Eisen | Balance | ||
Kobalt | 9 % Show Supplier Material materials with Kobalt of 9 % | ||
Molybdän | 5 % Show Supplier Material materials with Molybdän of 5 % | ||
Nickel | 4 % Show Supplier Material materials with Nickel of 4 % | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | In heat-treated, hardened condition (up to 69 HRC), Ferro-Titanit® can be used to solve many wear problems economically. | |
| General machinability | In as-delivered condition, this material can be machined by conventional methods. | |
| Heat Treatment | Annealing: 850°C, 2-4 hr in vacuum (Cooling 1-4.5 bar N2) Hardness: 53 HRC - Age-Hardening 480°C, 6-8 hr, Hardness: 62 HRC | |