Nickel 99.98% Rod & Wire Full Hard

Alternative und Handelsbezeichungen
N02270, 2.4050, N02200, N02201, 2.4060, 2.4061, 2.4066, 2.4068, N02205, Pure Nickel

Want to keep this datasheet? Save it now in your required format

Description

Nickel with highest degree of purity with the following features:

Very low levels of carbon (20 ppm) and sulfur (2 ppm) which tend to segregate at grain boundries resulting in hot shortening

Cleanliness, absence of non-metallic inclusions as Al, Ti or Si oxides

Low electrical resistivity at 20°C

High thermal conductivity at 20°C

Excellent formability

Low softening temperature (350°C)

Low recrystallization temperature (350°C)

Improved oxidation resistance: development of tightly adherent one-layer oxide scale instead of a two-layer costumary one, which tends to flake off due to mismatch in thermal expansion.

Equivalent Materials

Diese Materialdaten wurden von Hpulcas GmbH zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Eigenschaften

Abmessung

Property	Value
Dimensions	Rod: Diameter: up to 4.7 mm, Length: up to 2500 mm - Wire: Diameter: 0.2-1.6 mm ; various dimensions can be also customized

Mechanisch

Property	Temperature	Value	Comment
Elastizitätsmodul	23.0 °C	196 GPa Show Supplier Material materials with Elastizitätsmodul of 196 GPa
Härte, Vickers	23.0 °C	150 [-] Show Supplier Material materials with Härte, Vickers of 150 [-]	min.

Thermisch

Property	Temperature	Value
Recrystallization temperature		350 °C Show Supplier Material materials with Recrystallization temperature of 350 °C
Wärmeleitfähigkeit	23.0 °C	90.9 - 91 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 90.9 - 91 W/(m·K)

Elektrisch

Property	Temperature	Value
spezifischer Widerstand	23.0 °C	7.1E-8 Ω·m Show Supplier Material materials with spezifischer Widerstand of 7.1E-8 Ω·m

Chemical properties

Property	Value
Kohlenstoff	2E-3 % Show Supplier Material materials with Kohlenstoff of 2E-3 %
Nickel	99.98 % Show Supplier Material materials with Nickel of 99.98 %
Schwefel	2E-4 % Show Supplier Material materials with Schwefel of 2E-4 %

Technological properties

Property
Application areas	Wire: Sputter Targets, evaporation pellets, regulator coil in glow plugs of diesel engines; litz wire for current conduction under elevated temperatures and in aggressive environments, Pre material for thin wire manfacturing, Ni wire mesh, Thermal Spraying, Coating layer for corrosion protection from alkalis; salt spray; molten salt and reduciing chemicals; coating layer for high temperature resistance; corrosion protection at high temperatures; coating layer for membrane walls of power plants
Heat Treatment	Full Hardened
Processing history	For producing wire, the 6 mm hot rolled thick plates are cut into 6 mm wide sticks. The sticks are frontally welded. Afterwards the raw wire can be treated in the same way as hot rolled wire produced by melt metallurgy. accordingly, the wire is drawn to the desired dimensions through cold drawing and intermediate annealing.
Surface Finish	Blank/Bare/bright surface