Eigenschaften
Allgemein
| Property | Temperature | Value |
|---|---|---|
Dichte | 23.0 °C | 8 g/cm³ Show Supplier Material materials with Dichte of 8 g/cm³ |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung A5 | 23.0 °C | 28 % Show Supplier Material materials with Dehnung A5 of 28 % | min. |
Elastizitätsmodul | 23.0 °C | 200 GPa Show Supplier Material materials with Elastizitätsmodul of 200 GPa | |
Härte, Brinell | 23.0 °C | 215 [-] Show Supplier Material materials with Härte, Brinell of 215 [-] | max. |
Streckgrenze Rp 0,2 | 23.0 °C | 200 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 200 MPa | min. |
Zugfestigkeit | 23.0 °C | 500 - 700 MPa Show Supplier Material materials with Zugfestigkeit of 500 - 700 MPa |
Thermisch
| Property | Temperature | Value |
|---|---|---|
Spezifische Wärmekapazität | 23.0 °C | 500 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 500 J/(kg·K) |
Wärmeleitfähigkeit | 23.0 °C | 15 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 15 W/(m·K) |
Elektrisch
| Property | Temperature | Value |
|---|---|---|
spezifischer Widerstand | 23.0 °C | 7.5E-7 Ω·m Show Supplier Material materials with spezifischer Widerstand of 7.5E-7 Ω·m |
Magnetisch
| Property | Value |
|---|---|
Magnetic properties | Magnetisation is not possible |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Chrom | 16.5 - 18.5 % Show Supplier Material materials with Chrom of 16.5 - 18.5 % | |
Kohlenstoff | 0.08 % Show Supplier Material materials with Kohlenstoff of 0.08 % | max. |
Mangan | 2 % Show Supplier Material materials with Mangan of 2 % | max. |
Molybdän | 2 - 2.5 % Show Supplier Material materials with Molybdän of 2 - 2.5 % | |
Nickel | 10.5 - 13.5 % Show Supplier Material materials with Nickel of 10.5 - 13.5 % | |
Phosphor | 0.04 % Show Supplier Material materials with Phosphor of 0.04 % | max. |
Schwefel | 0.015 - 0.03 % Show Supplier Material materials with Schwefel of 0.015 - 0.03 % | |
Silizium | 1 % Show Supplier Material materials with Silizium of 1 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Apparatus engineering, Chemical industry, Textile Industry, Food Technology, Mechanical Engineering, Ship building, Medical technology & pharmacy | |
| Corrosion properties | Very good | |
| General machinability | Medium-not good | |
| Solution annealing | 1020-1120°C | |
| Welding | TIG welding: suitable, MAG Solid wire: suitable, Arc welding: suitable, UP welding: suitable, Laser beam welding: suitable, Gas fusion welding: suitable. It has a tendency to hot crack formation. | |
| Workability | Hot forming: 900-1200°C | |