Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.17 g/cm³ Show Material materials with Dichte of 1.17 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.08 % Show Material materials with Wasserabsorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 69 MPa Show Material materials with Biegefestigkeit of 69 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 1.86 GPa Show Material materials with Biegemodul of 1.86 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 122.4 % Show Material materials with Dehnung of 122.4 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 1.83 GPa Show Material materials with Elastizitätsmodul of 1.83 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 4.6 % Show Material materials with Elongation at yield of 4.6 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 71 MPa Show Material materials with Flexural yield strength of 71 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -40.0 °C | 598 J/m Show Material materials with Impact strength, Izod notched, ASTM of 598 J/m | ASTM D 256 |
-30.0 °C | 647 J/m Show Material materials with Impact strength, Izod notched, ASTM of 647 J/m | ASTM D 256 | |
-20.0 °C | 695 J/m Show Material materials with Impact strength, Izod notched, ASTM of 695 J/m | ASTM D 256 | |
-10.0 °C | 663 J/m Show Material materials with Impact strength, Izod notched, ASTM of 663 J/m | ASTM D 256 | |
23.0 °C | 722 J/m Show Material materials with Impact strength, Izod notched, ASTM of 722 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 47 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 47 kJ/m² | ISO 179/1eA |
23.0 °C | 55 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 55 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 46 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 46 kJ/m² | ISO 180/1A |
-30.0 °C | 48 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 48 kJ/m² | ISO 180/1A | |
-20.0 °C | 50 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 50 kJ/m² | ISO 180/1A | |
-10.0 °C | 52 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 52 kJ/m² | ISO 180/1A | |
23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 55 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 44 MPa Show Material materials with Streckgrenze of 44 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 50 MPa Show Material materials with Zugfestigkeit of 50 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 109 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 109 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9.75E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9.75E-5 1/K | ASTM E 831 | -40°C to 95°C |
Vicat-Erweichungstemperatur | 119 °C Show Material materials with Vicat-Erweichungstemperatur of 119 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ASTM E 831 | -40°C to 95°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 11 g/10min Show Material materials with Schmelzmassenflussrate of 11 g/10min | ISO 1133 | 250°C/5 kg | |
Schmelzvolumenflussrate | 18 cm³/10min Show Material materials with Schmelzvolumenflussrate of 18 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 1 - 1.2 % Show Material materials with Schrumpfung of 1 - 1.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine,Auto Aftermarket,City,Data Transfer,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior Rail Components,Heavy Vehicles,Individual Equiptment,Industrial Material Handling,Lab Ware and Clinical Diagnostics,Lawn/Garden,Medical Device,Motorcycle,Rear/Signal Lighting,Security/Detection,Wireless Communications,Wire & cable | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |