Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Material materials with Dichte of 1.22 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.05 % Show Material materials with Wasserabsorption of 0.05 % | ISO 62 | 23°C, 50% RH |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.05 GPa Show Material materials with Biegemodul of 2.05 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 150 % Show Material materials with Dehnung of 150 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.1 GPa Show Material materials with Elastizitätsmodul of 2.1 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 600 J/m Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | ||
23.0 °C | 750 J/m Show Material materials with Impact strength, Izod notched, ASTM of 750 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 60 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 60 kJ/m² | ISO 179/1eA | ||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 25 kJ/m² | ISO 180/1A | ||
23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 55 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 50 MPa Show Material materials with Streckgrenze of 50 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No break @ -30°C | ISO 179/2C | ||||
Schlagzähigkeit, Izod ungekerbt | No break @ -40°C | ISO 180/1U |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 105 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 105 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 125 °C Show Material materials with Vicat-Erweichungstemperatur of 125 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 9E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 260.0 °C | 260 Pa·s Show Material materials with Melt viscosity of 260 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzmassenflussrate | 11 g/10min Show Material materials with Schmelzmassenflussrate of 11 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Schmelzvolumenflussrate | 10 cm³/10min Show Material materials with Schmelzvolumenflussrate of 10 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.7 - 1.1 % Show Material materials with Schrumpfung of 0.7 - 1.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C |