Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Material materials with Dichte of 1.2 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Wasseraufnahme, Gleichgewicht | 100.0 °C | 0.58 % Show Material materials with Wasseraufnahme, Gleichgewicht of 0.58 % | ASTM D 570 | ASTM D 570 |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.3 GPa Show Material materials with Biegemodul of 2.3 GPa | ISO 178 | 2 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.35 GPa Show Material materials with Elastizitätsmodul of 2.35 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 150 J/m Show Material materials with Impact strength, Izod notched, ASTM of 150 J/m | ASTM D 256 | ||
23.0 °C | 750 J/m Show Material materials with Impact strength, Izod notched, ASTM of 750 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 50 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 50 kJ/m² | ISO 179/1eA | ||
23.0 °C | 70 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 70 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 55 kJ/m² | ISO 180/1A | ||
23.0 °C | 75 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 75 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 65 MPa Show Material materials with Zugfestigkeit of 65 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23,-30°C | ASTM D 4812 | ||||
Schlagzähigkeit, Charpy ungekerbt | No break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No break @ 23,-30°C | ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 145 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ASTM E 831 | -40°C to 95°C |
Schmelzpunkt | 265 - 275 °C Show Material materials with Schmelzpunkt of 265 - 275 °C | ||
Spezifische Wärmekapazität | 23.0 °C | 1250 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 1250 J/(kg·K) | ASTM C 351 |
Vicat-Erweichungstemperatur | 150 °C Show Material materials with Vicat-Erweichungstemperatur of 150 °C | ASTM D 1525 | Rate B/50 | |
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 |
Optisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 2.5 g/10min Show Material materials with Schmelzmassenflussrate of 2.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schmelzvolumenflussrate | 4 cm³/10min Show Material materials with Schmelzvolumenflussrate of 4 cm³/10min | ISO 1133 | 300°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Bottles,Document Handling,Food Container,Industrial Material Handling,Medical Device,Pharmaceutical Packaging & Drug Delivery,Wire & cable | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 320-345°C, Nozzle Temperature: 315-340°C, Front - Zone 3 Temperature: 320-345°C, Middle - Zone 2 Temperature: 310-330°C, Rear - Zone 1 Temperature: 300-320°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm, Drying Temperature: 115-120°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Minimum Moisture Content: 0.01%, Barrel - Zone 1 Temperature: 260-275°C, Barrel - Zone 2 Temperature: 260-275°C, Barrel - Zone 3 Temperature: 260-275°C, Barrel - Zone 4 Temperature: 260-275°C, Adapter - Zone 5 Temperature: 260-275°C, Head - Zone 6 - Top Temperature: 260-275°C, Head - Zone 7 - Bottom Temperature: 260-275°C, Screw Speed: 15-50rpm, Mold Temperature: 65-95°C, Die Temperature: 270-280°C | |