Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 78 MPa Show Material materials with Biegefestigkeit of 78 MPa | ISO 178 |
Biegemodul | 23.0 °C | 1.7 GPa Show Material materials with Biegemodul of 1.7 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 150 % Show Material materials with Dehnung of 150 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 1.52 GPa Show Material materials with Elastizitätsmodul of 1.52 GPa | ASTM D 638 | 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 71 MPa Show Material materials with Flexural yield strength of 71 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Härte, Shore D | 23.0 °C | 73 [-] Show Material materials with Härte, Shore D of 73 [-] | ASTM D 2240 |
Impact strength, Izod notched, ASTM | -30.0 °C | 73 J/m Show Material materials with Impact strength, Izod notched, ASTM of 73 J/m | ASTM D 256 |
23.0 °C | 1120 J/m Show Material materials with Impact strength, Izod notched, ASTM of 1120 J/m | ASTM D 256 | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A |
-10.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | |
23.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 47 MPa Show Material materials with Streckgrenze of 47 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 46 MPa Show Material materials with Zugfestigkeit of 46 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 75 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 75 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.05E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.05E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 91 °C Show Material materials with Vicat-Erweichungstemperatur of 91 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.23 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.23 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.05E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.05E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94V-2 Flame Class Rating | 3mm | UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 0 V Show Material materials with Kriechstromfestigkeit of 0 V | UL 746A |
Optisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 15 g/10min Show Material materials with Schmelzmassenflussrate of 15 g/10min | ASTM D 1238 | 265°C/2.16kgf | |
Schmelzvolumenflussrate | 15 cm³/10min Show Material materials with Schmelzvolumenflussrate of 15 cm³/10min | ISO 1133 | 265°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.8 % Show Material materials with Schrumpfung of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.4 - 0.6 % Show Material materials with Schrumpfung, diagonal of 0.4 - 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Amusement Machine,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,EV Infrastructure,Lab Ware and Clinical Diagnostics,Laundry Dryer,LED Lighting,Medical Device,Medical Facility Infrastructure,Non-LED Lighting,Personal Care,Plumbing,Respiratory,Safety Glasses,Surgical Devices,Swimming Pool/Spa,Washing Machine | |
Processing methods | Drying Temperature: 65-75°C, Drying Time: 3-5hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-265°C, Nozzle Temperature: 245-265°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-260°C, Rear - Zone 1 Temperature: 240-250°C, Mold Temperature: 45-60°C, Back Pressure: 0.2-0.5MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.02mm |