Zytel® 101L BKB009

Want to keep this datasheet? Save it now in your required format

Description

Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured. The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.Zytel® 101LBKB009 is a lubricated polyamide 66 resin for injection molding.

Equivalent Materials

Diese Materialdaten wurden von Matmatch zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.14 g/cm³ Show Material materials with Dichte of 1.14 g/cm³	ISO 1183

Mechanisch

Property	Temperature	Value	Comment
Biegemodul	23.0 °C	2.8 GPa Show Material materials with Biegemodul of 2.8 GPa	ISO 178
Dehnung	23.0 °C	16 % Show Material materials with Dehnung of 16 %	ISO 527-1/-2
Elastizitätsmodul	23.0 °C	3.05 GPa Show Material materials with Elastizitätsmodul of 3.05 GPa	ISO 527-1/-2
Elongation at yield	23.0 °C	4.6 % Show Material materials with Elongation at yield of 4.6 %	ISO 527-1/-2
Poissonzahl	23.0 °C	0.37 [-] Show Material materials with Poissonzahl of 0.37 [-]
Schlagfestigkeit, Charpy gekerbt	-6.0 °C	3.7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3.7 kJ/m²	ISO 179/1eA
	23.0 °C	4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m²	ISO 179/1eA

Schlagzähigkeit, Charpy ungekerbt	-6.0 °C	134 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 134 kJ/m²	ISO 179/1eU
	23.0 °C	203 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 203 kJ/m²	ISO 179/1eU
	Unlock all property charts
Streckgrenze	23.0 °C	88 MPa Show Material materials with Streckgrenze of 88 MPa	ISO 527-1/-2

Thermisch

Property	Value	Comment
Glasübergangstemperatur	65 °C Show Material materials with Glasübergangstemperatur of 65 °C	ISO 11357-1/-2 \| 18°F/min
Heat deflection temperature, 0.45 MPa	190 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 190 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa	70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C	ISO 75-1/-2
Relative temperature index, electrical	130 °C Show Material materials with Relative temperature index, electrical of 130 °C	UL 746B \| 240mil
Relative temperature index, mechanical impact	75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C	UL 746B \| 240mil
Relative temperature index, mechanical strength	85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C	UL 746B \| 240mil
Schmelzpunkt	262 °C Show Material materials with Schmelzpunkt of 262 °C	ISO 11357-1/-3 \| 18°F/min
Entflammbarkeit	Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Technological properties

Property
Processing methods	Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C

Zytel® 101L BKB009

Description

Equivalent Materials

Ashby charts

Empfohlene Literatur

Eigenschaften