| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.56 g/cm³ Show Material materials with Dichte of 1.56 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 2.3 % Show Material materials with Dehnung of 2.3 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 11 GPa Show Material materials with Elastizitätsmodul of 11 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Zugfestigkeit | 23.0 °C | 170 MPa Show Material materials with Zugfestigkeit of 170 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.8E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Schmelzpunkt | 252 °C Show Material materials with Schmelzpunkt of 252 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 1500 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 1500 J/(kg·K) | of melt | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.1E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at thickness h: HB class, Thickness tested: 0.85 mm, UL recognition: yes -, Glow Wire Flammability Index, 120mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 36 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.2 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.2 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 1.4E-3 [-] Show Material materials with Dissipation factor, 100Hz of 1.4E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 38 kV/mm Show Material materials with Durchschlagfestigkeit of 38 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 200 V Show Material materials with Kriechstromfestigkeit of 200 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 9 g/10min Show Material materials with Schmelzmassenflussrate of 9 g/10min | ISO 1133 | 280°C/2.16kg | |
Schrumpfung | 23.0 °C | 0.1 % Show Material materials with Schrumpfung of 0.1 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 0.6 % Show Material materials with Schrumpfung, diagonal of 0.6 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 140°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |