Zytel® HTN53G60LRHF BK083

Alternative und Handelsbezeichungen
PA-GF60

Want to keep this datasheet? Save it now in your required format

Description

Zytel® HTN high performance polyamide resins feature high retention of properties upon exposure to elevated temperature, to high moisture, and to harsh chemical environments. Polymer families and grades of Zytel® HTN are tailored to optimize performance as well as processability. Typical applications with Zytel® HTN include demanding applications in the automotive, electrical and electronics, domestic appliances, and construction industries. Zytel® HTN53G60LRHF BK083 is a 60% glass reinforced, lubricated, high performance polyamide resin with improved flow. It was developed for structural applications requiring excellent surface appearance using water-heated molds.

Equivalent Materials

Diese Materialdaten wurden von Matmatch zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.72 g/cm³ Show Material materials with Dichte of 1.72 g/cm³	ISO 1183

Mechanisch

Property	Temperature	Value	Comment
Biegefestigkeit	23.0 °C	405 MPa Show Material materials with Biegefestigkeit of 405 MPa	ISO 178
Biegemodul	23.0 °C	19.1 GPa Show Material materials with Biegemodul of 19.1 GPa	ISO 178
Dehnung	23.0 °C	2.2 % Show Material materials with Dehnung of 2.2 %	ISO 527-1/-2
Elastizitätsmodul	23.0 °C	21 GPa Show Material materials with Elastizitätsmodul of 21 GPa	ISO 527-1/-2
Poissonzahl	23.0 °C	0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]
Schlagfestigkeit, Charpy gekerbt	-6.0 °C	17 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 17 kJ/m²	ISO 179/1eA
	23.0 °C	16 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m²	ISO 179/1eA

Schlagzähigkeit, Charpy ungekerbt	23.0 °C	90 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m²	ISO 179/1eU
Zugfestigkeit	23.0 °C	265 MPa Show Material materials with Zugfestigkeit of 265 MPa	ISO 527-1/-2

Thermisch

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	255 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 255 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa	245 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 245 °C	ISO 75-1/-2
Schmelzpunkt	260 °C Show Material materials with Schmelzpunkt of 260 °C	ISO 11357-1/-3 \| first heat
Entflammbarkeit	Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

Property	Temperature	Value	Comment
Schrumpfung	23.0 °C	0.1 % Show Material materials with Schrumpfung of 0.1 %	ISO 294-4, 2577
Schrumpfung, diagonal	23.0 °C	0.5 % Show Material materials with Schrumpfung, diagonal of 0.5 %	ISO 294-4, 2577

Technological properties

Property
Fillers	60% Glass Fiber
Processing methods	Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Min. mold temperature: 90°C, Max. mold temperature: 110°C