Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.14 g/cm³ Show Material materials with Dichte of 1.14 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 8.5 % Show Material materials with Wasserabsorption of 8.5 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 3 GPa Show Material materials with Elastizitätsmodul of 3 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | ||
23.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | |||
Streckgrenze | 23.0 °C | 82 MPa Show Material materials with Streckgrenze of 82 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 205 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 205 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 74 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 74 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat-Erweichungstemperatur | 245 °C Show Material materials with Vicat-Erweichungstemperatur of 245 °C | ISO 306 | 90°F/h, 11 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | FMVSS Class: DNI | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schrumpfung | 23.0 °C | 1.5 % Show Material materials with Schrumpfung of 1.5 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C | |