Allgemein
Property | Value | Comment |
---|---|---|
Carbon equivalent (CET) | 0.32 [-] Show Material materials with Carbon equivalent (CET) of 0.32 [-] | |
Carbon equivalent (CEV) | 0.46 [-] Show Material materials with Carbon equivalent (CEV) of 0.46 [-] | for t ≤ 50 mm plate thickness |
0.48 [-] Show Material materials with Carbon equivalent (CEV) of 0.48 [-] | for 50 < t ≤100 mm plate thickness | |
0.5 [-] Show Material materials with Carbon equivalent (CEV) of 0.5 [-] | for 100 < t ≤ 250 mm plate thickness | |
Dichte | 7.8 - 7.9 g/cm³ Show Material materials with Dichte of 7.8 - 7.9 g/cm³ | typical for low carbon steel |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | -40 °C | 50 J Show Material materials with Charpy impact energy, V-notch of 50 J | min. |
Charpy impact energy, V-notch, transverse | -40 °C | 33 J Show Material materials with Charpy impact energy, V-notch, transverse of 33 J | min. |
Dehnung | 17 % Show Material materials with Dehnung of 17 % | min., Transverse | |
19 % Show Material materials with Dehnung of 19 % | min. | ||
Elastizitätsmodul | 200 - 215 GPa Show Material materials with Elastizitätsmodul of 200 - 215 GPa | typical for low carbon steel | |
Poissonzahl | 0.29 [-] Show Material materials with Poissonzahl of 0.29 [-] | typical for low carbon steel | |
Schubmodule | 82 GPa Show Material materials with Schubmodule of 82 GPa | typical for low carbon steel | |
Zugfestigkeit | 610 - 770 MPa Show Material materials with Zugfestigkeit of 610 - 770 MPa |
Thermisch
Property | Value | Comment |
---|---|---|
Koeffizient der thermischen Ausdehnung | 1.32e-05 - 1.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.32e-05 - 1.38e-05 1/K | typical for low carbon steel |
Max. Betriebstemperatur | 500 °C Show Material materials with Max. Betriebstemperatur of 500 °C | typical for carbon steel |
Schmelzpunkt | 1480 - 1526 °C Show Material materials with Schmelzpunkt of 1480 - 1526 °C | typical for low carbon steel |
Spezifische Wärmekapazität | 465 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 465 J/(kg·K) | typical for low carbon steel |
Wärmeleitfähigkeit | 25 - 93 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 25 - 93 W/(m·K) | typical for low carbon steel |
Elektrisch
Property | Value | Comment |
---|---|---|
spezifischer Widerstand | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with spezifischer Widerstand of 1.43e-07 - 1.74e-07 Ω·m | typical for carbon steel |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % | min. |
Chrom | 0.5 % Show Material materials with Chrom of 0.5 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Kohlenstoff | 0.14 % Show Material materials with Kohlenstoff of 0.14 % | |
Kupfer | 0.55 % Show Material materials with Kupfer of 0.55 % | |
Mangan | 1 - 1.7 % Show Material materials with Mangan of 1 - 1.7 % | |
Molybdän | 0.5 % Show Material materials with Molybdän of 0.5 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Nickel | 2 % Show Material materials with Nickel of 2 % | higher Ni content may be qualified and accepted subject to qualification during manufacturer qualification testing |
Niobium | 0.05 % Show Material materials with Niobium of 0.05 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Phosphor | 0.02 % Show Material materials with Phosphor of 0.02 % | |
Sauerstoff | 0.005 % Show Material materials with Sauerstoff of 0.005 % | |
Schwefel | 0.01 % Show Material materials with Schwefel of 0.01 % | |
Silizium | 0.6 % Show Material materials with Silizium of 0.6 % | |
Stickstoff | 0.025 % Show Material materials with Stickstoff of 0.025 % | the total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used, the minimum Al value and Al/N ratio do not apply |
Titan | 0.05 % Show Material materials with Titan of 0.05 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Vanadium | 0.12 % Show Material materials with Vanadium of 0.12 % | total Nb+V+Ti ≤ 0.26% and Mo+Cr ≤ 0.65% |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |