DIN 17465 Grade GX40CrNiSi25-20 cast condition

Want to keep this datasheet? Save it now in your required format

Description

G-X 40 CrNiSi 25 20, for parts of ovens with highest mechanical loadings, previously loaded to high heat resistance, like transport elements in oven for annealing, tempering, sheet normalising and throughput, this are for example rolls, bearing arbor, bearing grate, bolts, anchor, lever, oven plates, burner, chains, snail retorts, transport rolls. Furthermore for insert boxes, annealing boxes, mortar trough, annealing hood, saucer, caps, burn roods and bearing stator. resistance: - in oxidising burning atmosphere: 1150°C - in reductive burning atmosphere: sensitive for carborising, especially upper 900°C - in oxidising sulfureous gas: in limited case - in reductive sulfureous gas: unresistant

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value
Dichte	20.0 °C	7.9 g/cm³ Show Material materials with Dichte of 7.9 g/cm³

Mechanisch

Property	Temperature	Value	Comment
Dehnung	20.0 °C	6 % Show Material materials with Dehnung of 6 %
Elastizitätsmodul	20.0 °C	200 GPa Show Material materials with Elastizitätsmodul of 200 GPa
Poissonzahl	23.0 °C	0.3 [-] Show Material materials with Poissonzahl of 0.3 [-]	Typical for Austenitic Stainless Steel
Schubmodule	23.0 °C	77 GPa Show Material materials with Schubmodule of 77 GPa	Typical for Austenitic Stainless Steel
Streckgrenze Rp 0,2	20.0 °C	230 MPa Show Material materials with Streckgrenze Rp 0,2 of 230 MPa
Zugfestigkeit	20.0 °C	440 MPa Show Material materials with Zugfestigkeit of 440 MPa

Thermisch

Property	Temperature	Value	Comment
Koeffizient der thermischen Ausdehnung	400.0 °C	1.7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.7E-5 1/K
	800.0 °C	1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.8E-5 1/K
	1000.0 °C	1.9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.9E-5 1/K
	1200.0 °C	1.95E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.95E-5 1/K

Max. Betriebstemperatur, lang		0 - 1150 °C Show Material materials with Max. Betriebstemperatur, lang of 0 - 1150 °C
Schmelzpunkt		1230 - 1480 °C Show Material materials with Schmelzpunkt of 1230 - 1480 °C	Typical for Austenitic Stainless Steel
Spezifische Wärmekapazität	20.0 °C	500 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 500 J/(kg·K)
Wärmeleitfähigkeit	20.0 °C	14.6 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 14.6 W/(m·K)

Elektrisch

Property	Temperature	Value
spezifischer Widerstand	20.0 °C	8.6E-7 Ω·m Show Material materials with spezifischer Widerstand of 8.6E-7 Ω·m

Chemical properties

Property	Value
Chrom	24 - 26 % Show Material materials with Chrom of 24 - 26 %
Kohlenstoff	0.3 - 0.5 % Show Material materials with Kohlenstoff of 0.3 - 0.5 %
Mangan	1.5 % Show Material materials with Mangan of 1.5 %
Nickel	19 - 21 % Show Material materials with Nickel of 19 - 21 %
Phosphor	0.04 % Show Material materials with Phosphor of 0.04 %
Schwefel	0.03 % Show Material materials with Schwefel of 0.03 %
Silizium	1 - 2.5 % Show Material materials with Silizium of 1 - 2.5 %