Allgemein
| Property | Temperature | Value |
|---|---|---|
Dichte | 20.0 °C | 7 g/cm³ Show Material materials with Dichte of 7 g/cm³ |
Mechanisch
| Property | Temperature | Value |
|---|---|---|
Compressive yield strength | 20.0 °C | 2200 MPa Show Material materials with Compressive yield strength of 2200 MPa |
Dehnung | 20.0 °C | 1 % Show Material materials with Dehnung of 1 % |
Elastizitätsmodul | 20.0 °C | 165 GPa Show Material materials with Elastizitätsmodul of 165 GPa |
Härte, Brinell | 20.0 °C | 250 - 480 [-] Show Material materials with Härte, Brinell of 250 - 480 [-] |
Plane-Strain Fracture Toughnes | 20.0 °C | 50 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 50 MPa·√m |
Poissonzahl | 20.0 °C | 0.27 [-] Show Material materials with Poissonzahl of 0.27 [-] |
Scherfestigkeit | 20.0 °C | 1260 MPa Show Material materials with Scherfestigkeit of 1260 MPa |
Schubmodule | 20.0 °C | 63 GPa Show Material materials with Schubmodule of 63 GPa |
Streckgrenze Rp 0,2 | 20.0 °C | 1100 MPa Show Material materials with Streckgrenze Rp 0,2 of 1100 MPa |
Torsion Strength | 20.0 °C | 1260 MPa Show Material materials with Torsion Strength of 1260 MPa |
Zugfestigkeit | 20.0 °C | 1360 - 1400 MPa Show Material materials with Zugfestigkeit of 1360 - 1400 MPa |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 200.0 °C | 1.4E-5 - 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.4E-5 - 1.8E-5 1/K | |
Schmelzpunkt | 1150 - 1200 °C Show Material materials with Schmelzpunkt of 1150 - 1200 °C | Typical for Ductile (Nodular) Cast Iron | |
Spezifische Wärmekapazität | 23.0 °C | 460 - 502 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 460 - 502 J/(kg·K) | Typical for Ductile (Nodular) Cast Iron |
Wärmeleitfähigkeit | 200.0 °C | 20 - 23 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 20 - 23 W/(m·K) |