Eigenschaften
Allgemein
| Property | Value | Condition |
|---|---|---|
Dichte | 2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | H116 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 160.0 MPa Show Material materials with Bending Fatigue Strength of 160.0 MPa | H116 | AA Standards | |
Dehnung | 13.0 % Show Material materials with Dehnung of 13.0 % | H116 | ||
14.0 % Show Material materials with Dehnung of 14.0 % | H116 | AA Standards | A100 | |
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | H116 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Streckgrenze | 230.0 MPa Show Material materials with Streckgrenze of 230.0 MPa | H116 | AA Standards | RP02 |
230.0 MPa Show Material materials with Streckgrenze of 230.0 MPa | H116 | |||
Zugfestigkeit | 315.0 MPa Show Material materials with Zugfestigkeit of 315.0 MPa | H116 | AA Standards | |
330.0 MPa Show Material materials with Zugfestigkeit of 330.0 MPa | H116 |
Thermisch
| Property | Value | Condition | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | H116 | |
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |
Schmelzpunkt | 580.0 °C Show Material materials with Schmelzpunkt of 580.0 °C | H116 | |
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | H116 | |
Wärmeleitfähigkeit | 120.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 120.0 W/(m·K) | H116 |
Elektrisch
| Property | Value | Comment |
|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 - 31000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
spezifischer Widerstand | 3.3e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 92.4 - 95.6 % Show Material materials with Aluminium of 92.4 - 95.6 % | H116 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H116 | |
Chrom | 0.05 - 0.25 % Show Material materials with Chrom of 0.05 - 0.25 % | H116 | AA Standards |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | H116 | AA Standards |
0.4 % Show Material materials with Eisen of 0.4 % | H116 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H116 | AA Standards |
Magnesium | 4.0 - 4.9 % Show Material materials with Magnesium of 4.0 - 4.9 % | H116 | AA Standards |
Mangan | 0.4 - 1.0 % Show Material materials with Mangan of 0.4 - 1.0 % | H116 | AA Standards |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | H116 | AA Standards |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | H116 | AA Standards |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H116 | AA Standards |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor | |
| Workability | general (condition): acceptable (O), poor(H321, H116, H111) | |