Eigenschaften
Allgemein
| Property | Value | Condition | Shape |
|---|---|---|---|
Dichte | 2.81 g/cm³ Show Material materials with Dichte of 2.81 g/cm³ | T651 | |
2.81 g/cm³ Show Material materials with Dichte of 2.81 g/cm³ | T651 | Bar | |
3.1 g/cm³ Show Material materials with Dichte of 3.1 g/cm³ | T651 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 160.0 MPa Show Material materials with Bending Fatigue Strength of 160.0 MPa | T651 | AA Standards | |||
Dauerfestigkeit | 159 MPa Show Material materials with Dauerfestigkeit of 159 MPa | T651 | for 5x10⁸ cycles | |||
Dehnung | -195 °C | 9 % Show Material materials with Dehnung of 9 % | T651 | Elongation in 50 mm | ||
-80 °C | 11 % Show Material materials with Dehnung of 11 % | T651 | Elongation in 50 mm | |||
2.0 % Show Material materials with Dehnung of 2.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
4.0 % Show Material materials with Dehnung of 4.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
5.0 % Show Material materials with Dehnung of 5.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
6.0 % Show Material materials with Dehnung of 6.0 % | T651 | AA Standards, ASTM B209 | A100 | |||
7.0 % Show Material materials with Dehnung of 7.0 % | T651 | AA Standards, ASTM B211 | Bar | A50 | ||
7.4 % Show Material materials with Dehnung of 7.4 % | T651 | |||||
9.0 % Show Material materials with Dehnung of 9.0 % | T651 | AA Standards, ASTM B209 | A50 | |||
9.0 % Show Material materials with Dehnung of 9.0 % | T651 | AA Standards | A100 | |||
11.0 % Show Material materials with Dehnung of 11.0 % | T651 | AA Standards | A50 | |||
11.0 % Show Material materials with Dehnung of 11.0 % | T651 | |||||
0 °C | 11 % Show Material materials with Dehnung of 11 % | T651 | Elongation in 50 mm | |||
24 °C | 11 % Show Material materials with Dehnung of 11 % | T651 | Elongation in 50 mm | |||
100 °C | 14 % Show Material materials with Dehnung of 14 % | T651 | Elongation in 50 mm | |||
150 °C | 30 % Show Material materials with Dehnung of 30 % | T651 | Elongation in 50 mm | |||
205 °C | 55 % Show Material materials with Dehnung of 55 % | T651 | Elongation in 50 mm | |||
260 °C | 65 % Show Material materials with Dehnung of 65 % | T651 | Elongation in 50 mm | |||
315 °C | 70 % Show Material materials with Dehnung of 70 % | T651 | Elongation in 50 mm | |||
370 °C | 70 % Show Material materials with Dehnung of 70 % | T651 | Elongation in 50 mm | |||
Elastizitätsmodul | 72.0 GPa Show Material materials with Elastizitätsmodul of 72.0 GPa | T651 | Bar | |||
Härte, Brinell | 150.0 [-] Show Material materials with Härte, Brinell of 150.0 [-] | T651 | AA Standards | |||
150.0 [-] Show Material materials with Härte, Brinell of 150.0 [-] | T651 | 500 kg load, 10 mm ball | ||||
Kompressionsmodul | 72.4 MPa Show Material materials with Kompressionsmodul of 72.4 MPa | T651 | ||||
Plane-Strain Fracture Toughnes | -196 °C | 33.5 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 33.5 MPa·√m | T651 | For plate in T-L direction | ||
24.2 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.2 MPa·√m | T651 | |||||
24 °C | 32.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 32.3 MPa·√m | T651 | For plate in T-L direction | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | T651 | ||||
Scherfestigkeit | 331.0 MPa Show Material materials with Scherfestigkeit of 331.0 MPa | T651 | ||||
Schubmodule | 26.9 GPa Show Material materials with Schubmodule of 26.9 GPa | T651 | ||||
Streckgrenze | -196 °C | 634 MPa Show Material materials with Streckgrenze of 634 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 545 MPa Show Material materials with Streckgrenze of 545 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-28 °C | 517 MPa Show Material materials with Streckgrenze of 517 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
370.0 MPa Show Material materials with Streckgrenze of 370.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
400.0 MPa Show Material materials with Streckgrenze of 400.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
420.0 MPa Show Material materials with Streckgrenze of 420.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
425.0 MPa Show Material materials with Streckgrenze of 425.0 MPa | T651 | AA Standards, ASTM B211 | RP02 | |||
440.0 MPa Show Material materials with Streckgrenze of 440.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211 | RP02 | |||
455.0 MPa Show Material materials with Streckgrenze of 455.0 MPa | T651 | AA Standards, ASTM B211 | Bar | RP02 | ||
460.0 MPa Show Material materials with Streckgrenze of 460.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
470.0 MPa Show Material materials with Streckgrenze of 470.0 MPa | T651 | AA Standards, ASTM B209 | RP02 | |||
470.0 MPa Show Material materials with Streckgrenze of 470.0 MPa | T651 | |||||
505.0 MPa Show Material materials with Streckgrenze of 505.0 MPa | T651 | AA Standards | RP02 | |||
505.0 MPa Show Material materials with Streckgrenze of 505.0 MPa | T651 | |||||
24 °C | 503 MPa Show Material materials with Streckgrenze of 503 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 448 MPa Show Material materials with Streckgrenze of 448 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
149 °C | 186 MPa Show Material materials with Streckgrenze of 186 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
204 °C | 87 MPa Show Material materials with Streckgrenze of 87 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
316 °C | 45 MPa Show Material materials with Streckgrenze of 45 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
371 °C | 32 MPa Show Material materials with Streckgrenze of 32 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Zugfestigkeit | -195 °C | 703 MPa Show Material materials with Zugfestigkeit of 703 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 620 MPa Show Material materials with Zugfestigkeit of 620 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
460.0 MPa Show Material materials with Zugfestigkeit of 460.0 MPa | T651 | AA Standards, ASTM B209 | ||||
490.0 MPa Show Material materials with Zugfestigkeit of 490.0 MPa | T651 | AA Standards, ASTM B209 | ||||
495.0 MPa Show Material materials with Zugfestigkeit of 495.0 MPa | T651 | AA Standards, ASTM B209 | ||||
505.0 MPa Show Material materials with Zugfestigkeit of 505.0 MPa | T651 | AA Standards, ASTM B211 | ||||
515.0 MPa Show Material materials with Zugfestigkeit of 515.0 MPa | T651 | AA Standards, ASTM B211 | ||||
525.0 MPa Show Material materials with Zugfestigkeit of 525.0 MPa | T651 | AA Standards, ASTM B209 | ||||
530.0 MPa Show Material materials with Zugfestigkeit of 530.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211 | ||||
531.0 MPa Show Material materials with Zugfestigkeit of 531.0 MPa | T651 | Bar | ||||
540.0 MPa Show Material materials with Zugfestigkeit of 540.0 MPa | T651 | AA Standards, ASTM B209 | ||||
560.0 MPa Show Material materials with Zugfestigkeit of 560.0 MPa | T651 | |||||
570.0 MPa Show Material materials with Zugfestigkeit of 570.0 MPa | T651 | AA Standards | ||||
0 °C | 593 MPa Show Material materials with Zugfestigkeit of 593 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
24 °C | 572 MPa Show Material materials with Zugfestigkeit of 572 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 483 MPa Show Material materials with Zugfestigkeit of 483 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 215 MPa Show Material materials with Zugfestigkeit of 215 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 110 MPa Show Material materials with Zugfestigkeit of 110 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 75 MPa Show Material materials with Zugfestigkeit of 75 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 55 MPa Show Material materials with Zugfestigkeit of 55 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Value | Condition | Shape |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | T651 | |
2.35e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.35e-05 1/K | T651 | Bar | |
Schmelzpunkt | 477.0 °C Show Material materials with Schmelzpunkt of 477.0 °C | T651 | |
480.0 °C Show Material materials with Schmelzpunkt of 480.0 °C | T651 | ||
635.0 °C Show Material materials with Schmelzpunkt of 635.0 °C | T651 | Bar | |
Spezifische Wärmekapazität | 910.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 910.0 J/(kg·K) | T651 | |
Wärmeleitfähigkeit | 130.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 W/(m·K) | T651 | |
134.0 - 160.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 134.0 - 160.0 W/(m·K) | T651 | Bar |
Elektrisch
| Property | Value | Condition | Shape | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 19000000 S/m Show Material materials with Elektrische Leitfähigkeit of 19000000 S/m | T651 | Typical/derived value | |
Specific Electrical conductivity | 33.0 % IACS Show Material materials with Specific Electrical conductivity of 33.0 % IACS | T651 | Typical value | |
spezifischer Widerstand | 4.31e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.31e-08 Ω·m | T651 | Bar | |
5.22e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.22e-08 Ω·m | T651 | Typical value |
Chemical properties
| Property | Value | Condition | Shape | Related Standards | Comment |
|---|---|---|---|---|---|
Aluminium | 86.9 - 91.4 % Show Material materials with Aluminium of 86.9 - 91.4 % | T651 | |||
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T651 | Bar | Total | |
Chrom | 0.18 - 0.28 % Show Material materials with Chrom of 0.18 - 0.28 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | T651 | AA Standards, ASTM B209, ASTM B211 | ||
0.5 % Show Material materials with Eisen of 0.5 % | T651 | Bar | |||
Kupfer | 1.2 - 2.0 % Show Material materials with Kupfer of 1.2 - 2.0 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Mangan | 0.3 % Show Material materials with Mangan of 0.3 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Zink | 5.1 - 6.1 % Show Material materials with Zink of 5.1 - 6.1 % | T651 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Zirkonium | 0.25 % Show Material materials with Zirkonium of 0.25 % | T651 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): not suitable | |