Eigenschaften
Allgemein
| Property | Value |
|---|---|
Dichte | 8.8 g/cm³ Show Supplier Material materials with Dichte of 8.8 g/cm³ |
Abmessung
| Property | Value |
|---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Hot-dip tinned and electroplated strip available. |
Mechanisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Biegefestigkeit 180°, in longitudinaler Richtung | 1 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1 [-] | ASTM B820 | R365(1/2H) | bending thickness: <0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1.5 [-] | ASTM B820 | R415(H) | bending thickness: <0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1.5 [-] | ASTM B820 | R460(EH) | bending thickness: <0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 2 [-] | ASTM B820 | R480(SH) | bending thickness: <0.5 mm & bending width: 10 mm | |
Biegefähigkeit 180°, in transversaler Richtung | 1 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 1 [-] | ASTM B820 | R365(1/2H) | bending thickness: <0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 1.5 [-] | ASTM B820 | R415(H) | bending thickness: <0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 1.5 [-] | ASTM B820 | R460(EH) | bending thickness: <0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 2 [-] | ASTM B820 | R480(SH) | bending thickness: <0.5 mm & bending width: 10 mm | |
Biegefähigkeit 90°, in longitudinaler Richtung | 0 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0 [-] | EN ISO 7438 | R365(1/2H) | bending thickness: <0.5 mm & bending width: 10 mm |
0.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0.5 [-] | EN ISO 7438 | R415(H) | bending thickness: <0.5 mm & bending width: 10 mm | |
0.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0.5 [-] | EN ISO 7438 | R460(EH) | bending thickness: <0.5 mm & bending width: 10 mm | |
0.8 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0.8 [-] | EN ISO 7438 | R480(SH) | bending thickness: <0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 1.5 [-] | EN ISO 7438 | R530(XSH) | bending thickness: <0.5 mm & bending width: 10 mm | |
Biegefähigkeit 90°, in transversaler Richtung | 0 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 0 [-] | EN ISO 7438 | R365(1/2H) | bending thickness: <0.5 mm & bending width: 10 mm |
0.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 0.5 [-] | EN ISO 7438 | R415(H) | bending thickness: <0.5 mm & bending width: 10 mm | |
1 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1 [-] | EN ISO 7438 | R460(EH) | bending thickness: <0.5 mm & bending width: 10 mm | |
1.2 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1.2 [-] | EN ISO 7438 | R480(SH) | bending thickness: <0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 2 [-] | EN ISO 7438 | R530(XSH) | bending thickness: <0.5 mm & bending width: 10 mm | |
Dehnung | 1 % Show Supplier Material materials with Dehnung of 1 % | min. | R530(XSH), A50 | |
1 % Show Supplier Material materials with Dehnung of 1 % | min. | R550(SSH), A50 | ||
2 % Show Supplier Material materials with Dehnung of 2 % | min. | R460(EH), A50 | ||
2 % Show Supplier Material materials with Dehnung of 2 % | min. | R480(SH), A50 | ||
3 % Show Supplier Material materials with Dehnung of 3 % | min. | R415(H), A50 | ||
6 % Show Supplier Material materials with Dehnung of 6 % | min. | R365(1/2H), A50 | ||
Elastizitätsmodul | 121 GPa Show Supplier Material materials with Elastizitätsmodul of 121 GPa | ||
Härte, Vickers | 110 - 140 [-] Show Supplier Material materials with Härte, Vickers of 110 - 140 [-] | R365(1/2H) | For reference only | |
125 - 145 [-] Show Supplier Material materials with Härte, Vickers of 125 - 145 [-] | R415(H) | For reference only | ||
130 - 150 [-] Show Supplier Material materials with Härte, Vickers of 130 - 150 [-] | R460(EH) | For reference only | ||
135 - 155 [-] Show Supplier Material materials with Härte, Vickers of 135 - 155 [-] | R480(SH) | For reference only | ||
150 [-] Show Supplier Material materials with Härte, Vickers of 150 [-] | min. | R530(XSH) | For reference only | ||
155 [-] Show Supplier Material materials with Härte, Vickers of 155 [-] | min. | R550(SSH) | For reference only | ||
Poissonzahl | 0.33 [-] Show Supplier Material materials with Poissonzahl of 0.33 [-] | ||
Streckgrenze | 250 MPa Show Supplier Material materials with Streckgrenze of 250 MPa | min. | R365(1/2H) | |
365 MPa Show Supplier Material materials with Streckgrenze of 365 MPa | min. | R415(H) | ||
440 MPa Show Supplier Material materials with Streckgrenze of 440 MPa | min. | R460(EH) | ||
460 MPa Show Supplier Material materials with Streckgrenze of 460 MPa | min. | R480(SH) | ||
500 MPa Show Supplier Material materials with Streckgrenze of 500 MPa | min. | R530(XSH) | ||
520 MPa Show Supplier Material materials with Streckgrenze of 520 MPa | min. | R550(SSH) | ||
Zugfestigkeit | 365 - 435 MPa Show Supplier Material materials with Zugfestigkeit of 365 - 435 MPa | R365(1/2H) | |
415 - 485 MPa Show Supplier Material materials with Zugfestigkeit of 415 - 485 MPa | R415(H) | ||
460 - 505 MPa Show Supplier Material materials with Zugfestigkeit of 460 - 505 MPa | R460(EH) | ||
485 - 525 MPa Show Supplier Material materials with Zugfestigkeit of 485 - 525 MPa | R480(SH) |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1.76e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.76e-05 1/K | average value between 20-300°C | |
Spezifische Wärmekapazität | 385 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 385 J/(kg·K) | ||
Wärmeleitfähigkeit | 20 °C | 280 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 280 W/(m·K) |
Elektrisch
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Application target: Ideal for semiconductor. | |
| Chemical composition | The chemical composition is the nominal composition of the alloy | |
| Coating | Electroplating: Good Hot dip tinning: Very good | |
| Cold Forming | Good | |
| Machining | Not suitable | |
| Packaging size | Standard coils with outside diameters up to 1300 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
| Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
| Welding | Laser welding: Good Resistance welding: Good | |