Eigenschaften
Allgemein
| Property | Value |
|---|---|
Dichte | 8.9 g/cm³ Show Supplier Material materials with Dichte of 8.9 g/cm³ |
Abmessung
| Property | Value |
|---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Hot-dip tinned and electroplated strip available. |
Mechanisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Biegefestigkeit 180°, in longitudinaler Richtung | 1 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1 [-] | ASTM B820 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1.5 [-] | ASTM B820 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1.5 [-] | ASTM B820 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 2 [-] | ASTM B820 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Biegefähigkeit 180°, in transversaler Richtung | 1.5 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 1.5 [-] | ASTM B820 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 1.5 [-] | ASTM B820 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 2 [-] | ASTM B820 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 2 [-] | ASTM B820 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Biegefähigkeit 90°, in longitudinaler Richtung | 0.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0.5 [-] | EN ISO 7438 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 1 [-] | EN ISO 7438 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 1.5 [-] | EN ISO 7438 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 1.5 [-] | EN ISO 7438 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Biegefähigkeit 90°, in transversaler Richtung | 1 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1 [-] | EN ISO 7438 | R360(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1 [-] | EN ISO 7438 | R385(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1.5 [-] | EN ISO 7438 | R415(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 2 [-] | EN ISO 7438 | R440(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Dehnung | 1 % Show Supplier Material materials with Dehnung of 1 % | min. | R440(SH), A50 | |
2 % Show Supplier Material materials with Dehnung of 2 % | min. | R415(EH), A50 | ||
3 % Show Supplier Material materials with Dehnung of 3 % | min. | R385(H), A50 | ||
4 % Show Supplier Material materials with Dehnung of 4 % | min. | R360(3/4H), A50 | ||
Elastizitätsmodul | 125 GPa Show Supplier Material materials with Elastizitätsmodul of 125 GPa | ||
Härte, Vickers | 115 - 135 [-] Show Supplier Material materials with Härte, Vickers of 115 - 135 [-] | R360(3/4H) | For reference only | |
120 - 140 [-] Show Supplier Material materials with Härte, Vickers of 120 - 140 [-] | R385(H) | For reference only. | ||
125 - 145 [-] Show Supplier Material materials with Härte, Vickers of 125 - 145 [-] | R415(EH) | For reference only | ||
130 - 150 [-] Show Supplier Material materials with Härte, Vickers of 130 - 150 [-] | R440(SH) | For reference only | ||
Poissonzahl | 0.33 [-] Show Supplier Material materials with Poissonzahl of 0.33 [-] | ||
Streckgrenze | 345 MPa Show Supplier Material materials with Streckgrenze of 345 MPa | min. | R360(3/4H) | |
355 MPa Show Supplier Material materials with Streckgrenze of 355 MPa | min. | R385(H) | ||
400 MPa Show Supplier Material materials with Streckgrenze of 400 MPa | min. | R415(EH) | ||
425 MPa Show Supplier Material materials with Streckgrenze of 425 MPa | min. | R440(SH) | ||
Zugfestigkeit | 360 - 425 MPa Show Supplier Material materials with Zugfestigkeit of 360 - 425 MPa | R360(3/4H) | |
385 - 455 MPa Show Supplier Material materials with Zugfestigkeit of 385 - 455 MPa | R385(H) | ||
415 - 480 MPa Show Supplier Material materials with Zugfestigkeit of 415 - 480 MPa | R415(EH) | ||
440 - 510 MPa Show Supplier Material materials with Zugfestigkeit of 440 - 510 MPa | R440(SH) |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1.7e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.7e-05 1/K | average value between 20-300°C | |
Spezifische Wärmekapazität | 385 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 385 J/(kg·K) | ||
Wärmeleitfähigkeit | 20 °C | 350 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 350 W/(m·K) |
Elektrisch
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Application target: Ideal for semiconductor. | |
| Chemical composition | The chemical composition is the nominal composition of the alloy | |
| Coating | Electroplating: Good Hot dip tinning: Very good | |
| Cold Forming | Good | |
| Machining | Fair | |
| Packaging size | Standard coils with outside diameters up to 1300 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
| Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
| Welding | Laser welding: Average Resistance welding: Good | |