Allgemein
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Dichte | 1.41 g/cm³ Show Supplier Material materials with Dichte of 1.41 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 0.85 % Show Supplier Material materials with Moisture absorption of 0.85 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 1.9 % Show Supplier Material materials with Wasserabsorption of 1.9 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Biegefestigkeit | 280 MPa Show Supplier Material materials with Biegefestigkeit of 280 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 10.1 GPa Show Supplier Material materials with Biegemodul of 10.1 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 4.9 % Show Supplier Material materials with Dehnung of 4.9 % | dry | ISO 527-2/1A | 5mm/min | |
6.9 % Show Supplier Material materials with Dehnung of 6.9 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 9.8 GPa Show Supplier Material materials with Elastizitätsmodul of 9.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
11.5 GPa Show Supplier Material materials with Elastizitätsmodul of 11.5 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | dry | ISO 179/1eA | |
23 °C | 18 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 18 kJ/m² | dry | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 125 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 125 kJ/m² | dry | ISO 179/1eU | |
23 °C | 115 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 115 kJ/m² | dry | ISO 179/1eU | ||
Zugfestigkeit | 150 MPa Show Supplier Material materials with Zugfestigkeit of 150 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
185 MPa Show Supplier Material materials with Zugfestigkeit of 185 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1.8e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.8e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | ||
0.0001 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.0001 1/K | ISO 11359-1/-2 | ||||
Schmelzpunkt | 217 °C Show Supplier Material materials with Schmelzpunkt of 217 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 205 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 205 °C | ISO 75/2Af | 1.80 MPa | ||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Schrumpfung | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Hydrolysis Resistance, Heat Stabilized | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Molding |