Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.16 g/cm³ Show Supplier Material materials with Dichte of 1.16 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.7 % Show Supplier Material materials with Moisture absorption of 0.7 % | ISO 62 | (23°C / 50% RH) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 53 MPa Show Supplier Material materials with Biegefestigkeit of 53 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 1.2 GPa Show Supplier Material materials with Biegemodul of 1.2 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 200 % Show Supplier Material materials with Dehnung of 200 % | ASTM D 638 | brk, Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 1.2 GPa Show Supplier Material materials with Elastizitätsmodul of 1.2 GPa | ASTM D 638 | 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 500 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 500 J/m | ASTM D 256 | notched, 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 69 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 69 kJ/m² | ISO 179/2C | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 500 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 500 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 36 MPa Show Supplier Material materials with Zugfestigkeit of 36 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 83 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ASTM D 648 | 6.4 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 74 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 74 °C | ASTM D 648 | 6.4 mm, unannealed |
Wärmeformbeständigkeitstemperatur | 74 - 83 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 74 - 83 °C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.00E+11 - 5.00E+12 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+11 - 5.00E+12 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+11 - 5.00E+12 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+11 - 5.00E+12 Ω·cm | ASTM D 257 |
Optisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 19 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 19 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung, diagonal of 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Semiconductor, Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 90 to 95.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |