Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Relative Dichte | 23.0 °C | 1.26 [-] Show Supplier Material materials with Relative Dichte of 1.26 [-] | ASTM D 792 | |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 187 MPa Show Supplier Material materials with Biegefestigkeit of 187 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 11.6 GPa Show Supplier Material materials with Biegemodul of 11.6 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.9 % Show Supplier Material materials with Dehnung of 1.9 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 14.6 GPa Show Supplier Material materials with Elastizitätsmodul of 14.6 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 70 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 410 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 410 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/2C | 23°C |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 28 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 28 kJ/m² | ISO 179/2C | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 70 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 150 MPa Show Supplier Material materials with Zugfestigkeit of 150 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 117 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9.2E-6 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.2E-6 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 117 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 117 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.97E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.97E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101977560- - <br> UL Recognized, 94HB Flame Class Rating: ≥1mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 5000 - 500000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 5000 - 500000 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 5000 - 500000 Ω·cm Show Supplier Material materials with Volume resistivity of 5000 - 500000 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 34 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 34 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung, diagonal of 0.2 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 90 to 110.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |