Allgemein
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 98 MPa Show Supplier Material materials with Biegefestigkeit of 98 MPa | ISO 178 | ||
Biegemodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 6 % Show Supplier Material materials with Dehnung of 6 % | ISO 527 | yield | ||
Elastizitätsmodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Elastizitätsmodul of 2.2 GPa | ASTM D 638 | 50 mm/min | ||
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 750 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 750 J/m | ASTM D 256 | notched, 23°C | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 25 kJ/m² | ISO 179/2C | 23°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 75 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C | ||
Zugfestigkeit | 23.0 °C | 68 MPa Show Supplier Material materials with Zugfestigkeit of 68 MPa | ISO 527 | break | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 120 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 120 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Wärmeformbeständigkeitstemperatur | 120 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 120 °C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 3 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 1E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2E-3 [-] | ASTM D 150 |
Volume resistivity | 23.0 °C | 2.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+17 Ω·cm | ASTM D 257 |
Optisch
Property | Value | Comment |
---|---|---|
Brechungsindex | 1.59 [-] Show Supplier Material materials with Brechungsindex of 1.59 [-] | ISO 489 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 12 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 12 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |