Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Relative Dichte | 23.0 °C | 1.51 [-] Show Supplier Material materials with Relative Dichte of 1.51 [-] | ASTM D 792 |
Sauerstoffindex | 23.0 °C | 50 % Show Supplier Material materials with Sauerstoffindex of 50 % | |
Wasserabsorption | 23.0 °C | 0.9 % Show Supplier Material materials with Wasserabsorption of 0.9 % | ASTM D 570 | (23°C/Saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 227 MPa Show Supplier Material materials with Biegefestigkeit of 227 MPa | ASTM D 790 | brk, 2.6 mm/min, 100 mm span |
Biegemodul | 23.0 °C | 9 GPa Show Supplier Material materials with Biegemodul of 9 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Dehnung | 23.0 °C | 3 % Show Supplier Material materials with Dehnung of 3 % | ASTM D 638 | brk, Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 9.3 GPa Show Supplier Material materials with Elastizitätsmodul of 9.3 GPa | ASTM D 638 | 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 427 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 427 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 85 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 168 MPa Show Supplier Material materials with Zugfestigkeit of 168 MPa | ASTM D 638 | yld, Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 900 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 900 °C | IEC 60695-2-13 | 2.0 mm | |||
Heat deflection temperature, 0.45 MPa | 212 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 212 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.98E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.98E-5 1/K | ASTM E 831 | -20°C to 150°C | ||
Relative temperature index, electrical | 180 °C Show Supplier Material materials with Relative temperature index, electrical of 180 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 180 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 180 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 227 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 227 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 210 - 212 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 210 - 212 °C | ||||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=236984- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.38mm UL 94 <br> NBS Smoke Density, Flaming, Ds 4 min: 1.6- ASTM E 662 <br> UV-light, water exposure/immersion: F1- UL 746C | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 24.8 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 24.8 kV/mm | ASTM D 149 | in air, 1.6 mm |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
High Volt Arc Track Rate | 23.0 °C | 3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 1 |
Kriechstromfestigkeit | 23.0 °C | 4 V Show Supplier Material materials with Kriechstromfestigkeit of 4 V | UL 746A | (UL) {PLC} |
Verlustfaktor | 23.0 °C | 5.3E-3 [-] Show Supplier Material materials with Verlustfaktor of 5.3E-3 [-] | ASTM D 150 | 2450 MHz |
Volume resistivity | 23.0 °C | 3.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 3.00E+16 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method | on tensile bar |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Aircraft Seating, Air Cabin Interiors, Auto Aftermarket, Medical Facility Infrastructure, Surgical Devices | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 150°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |