Property | Temperature | Value | Comment |
---|---|---|---|
Relative Dichte | 23.0 °C | 0.99 [-] Show Supplier Material materials with Relative Dichte of 0.99 [-] | ASTM D 792 | |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 51 MPa Show Supplier Material materials with Biegefestigkeit of 51 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 1.4 GPa Show Supplier Material materials with Biegemodul of 1.4 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 75 % Show Supplier Material materials with Dehnung of 75 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 1.4 GPa Show Supplier Material materials with Elastizitätsmodul of 1.4 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 534 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 37 J Show Supplier Material materials with Instrumented Impact, Total Energy of 37 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 534 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 534 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 35 MPa Show Supplier Material materials with Zugfestigkeit of 35 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 112 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 112 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 85 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.62E-4 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.62E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 131 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 131 °C | ISO 306 | Rate A/50 | |||
Wärmeformbeständigkeitstemperatur | 85 - 112 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 85 - 112 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9.72E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 9.72E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221243- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 14 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 14 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Schmelzvolumenflussrate | 12 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 12 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung, diagonal of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Water Treatment/Filtration | |
Availability | Americas | |
Processing methods | Screw Speed: 20 to 100.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |