Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Supplier Material materials with Dichte of 1.22 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 290 MPa Show Supplier Material materials with Biegefestigkeit of 290 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 15.2 GPa Show Supplier Material materials with Biegemodul of 15.2 GPa | ISO 178 | 2 mm/min |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 243 MPa Show Supplier Material materials with Zugfestigkeit of 243 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 213 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 213 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Wärmeformbeständigkeitstemperatur | 213 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 213 °C |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |