Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 3.15 g/cm³ Show Supplier Material materials with Dichte of 3.15 g/cm³ | For ceramic structural parts |
Kristallgröße | 43169 μm Show Supplier Material materials with Kristallgröße of 43169 μm |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 480 MPa Show Supplier Material materials with Biegefestigkeit of 480 MPa | For ceramic structural parts |
Druckfestigkeit | 23.0 °C | 3500 MPa Show Supplier Material materials with Druckfestigkeit of 3500 MPa | For ceramic structural parts |
Elastizitätsmodul | 23.0 °C | 410 GPa Show Supplier Material materials with Elastizitätsmodul of 410 GPa | For ceramic structural parts |
Plane-Strain Fracture Toughnes | 23.0 °C | 4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 4 MPa·√m | For ceramic structural parts |
Poissonzahl | 23.0 °C | 0.21 [-] Show Supplier Material materials with Poissonzahl of 0.21 [-] | For ceramic structural parts |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.4E-6 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.4E-6 1/K | For ceramic structural parts |
Max. Betriebstemperatur | 1600 °C Show Supplier Material materials with Max. Betriebstemperatur of 1600 °C | For ceramic structural parts | |
Spezifische Wärmekapazität | 23.0 °C | 880 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 880 J/(kg·K) | For ceramic structural parts |
Wärmeleitfähigkeit | 23.0 °C | 150 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 150 W/(m·K) | For ceramic structural parts |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Used in semiconductor and coating industries, As a bearing material for magnetic drive pumps for many years. It is useful in a variety of applications including spray nozzles, shot blast nozzles and cyclone components | |
| Chemical composition | SiC, ZrO2, Si3N4 | |
| Processing history | Sintered | |