| Property | Value | Comment |
|---|---|---|
Recycled Content | 82.1 % Show Supplier Material materials with Recycled Content of 82.1 % | Average recycled content |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 35 % Show Supplier Material materials with Dehnung of 35 % | min. |
Streckgrenze Rp 0,2 | 23.0 °C | 205 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 205 MPa | min. |
Zugfestigkeit | 23.0 °C | 515 MPa Show Supplier Material materials with Zugfestigkeit of 515 MPa | min. |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Chrom | 22.5 % Show Supplier Material materials with Chrom of 22.5 % | ||
Eisen | Balance | ||
Kohlenstoff | 0.07 % Show Supplier Material materials with Kohlenstoff of 0.07 % | ||
Mangan | 1.7 % Show Supplier Material materials with Mangan of 1.7 % | ||
Nickel | 14 % Show Supplier Material materials with Nickel of 14 % | ||
Phosphor | 0.04 % Show Supplier Material materials with Phosphor of 0.04 % | max. | |
Schwefel | 0.015 % Show Supplier Material materials with Schwefel of 0.015 % | max. | |
Silizium | 0.5 % Show Supplier Material materials with Silizium of 0.5 % | ||
Technological properties
| Property | ||
|---|---|---|
| Welding | The weldability of Sandvik 8RE18 is good. Welding must be carried out without preheating and subsequent heat treatment is normally not required. Suitable methods of fusion welding are manual metal-arc welding (MMA/SMAW) and gas-shielded arc welding, with the TIG/GTAW method as first choice. For Sandvik 8RE18, heat input of <2.0 kJ/mm and interpass temperature of <150°C (300°F) are recommended. Recommended filler metals:
| |