Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23 °C | 2.8 GPa Show Supplier Material materials with Biegemodul of 2.8 GPa | ISO 527-2/2 |
Dehnung | 23 °C | 7 % Show Supplier Material materials with Dehnung of 7 % | ISO 527-2/50 |
Elastizitätsmodul | 23 °C | 2.7 GPa Show Supplier Material materials with Elastizitätsmodul of 2.7 GPa | ISO 527-2/2 |
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 12 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 12 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23 °C | 45 MPa Show Supplier Material materials with Zugfestigkeit of 45 MPa | ISO 527-2/50 |
Thermisch
Property | Value |
---|---|
Entflammbarkeit | UL94: HB |
Technological properties
Property | ||
---|---|---|
Certifications | ||
Fillers | 50% S-Wood Fiber | |
Other | General safety instructions, read also Process instructions: | |
Processing methods | Drying: 4 hours at 100°C 3D Extrusion DuraSense® 3D comes in pellet form and is meant to be used in extrusion deposition printing. It is important for optimal surface of the printed material that a significant pressure is built up behind the nozzle. This can be accomplished by setting the layer thickness higher than the actual nozzle diameter. Temperatures: DuraSense® can be melted around 170°C and processed up to 205°C. DuraSense® is sensitive to prolonged exposure to temperatures above 180°C. Avoid unnecessary heating and residence time. Do not set any zones above 205°C. Nozzle: DuraSense® 3D can be used with nozzle diameters equal to or larger than 2mm. |