Eigenschaften
Abmessung
| Property | Value |
|---|---|
Breite | 60 - 250 mm Show Supplier Material materials with Breite of 60 - 250 mm |
Dicke | 4 - 8 mm Show Supplier Material materials with Dicke of 4 - 8 mm |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Charpy impact energy, V-notch | -46.0 °C | 45 J Show Supplier Material materials with Charpy impact energy, V-notch of 45 J | |
Dehnung | 23.0 °C | 25 % Show Supplier Material materials with Dehnung of 25 % | |
Härte, Brinell | 23.0 °C | 290 [-] Show Supplier Material materials with Härte, Brinell of 290 [-] | |
Streckgrenze Rp 0,2 | 23.0 °C | 500 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 500 MPa | T<13MM |
Zugfestigkeit | 23.0 °C | 630 MPa Show Supplier Material materials with Zugfestigkeit of 630 MPa |
Chemical properties
| Property | Value |
|---|---|
Andere | B: 35 PPM |
Chrom | 22 - 24 % Show Supplier Material materials with Chrom of 22 - 24 % |
Eisen | Balance |
Kohlenstoff | 0.03 % Show Supplier Material materials with Kohlenstoff of 0.03 % |
Kupfer | 0.1 - 0.6 % Show Supplier Material materials with Kupfer of 0.1 - 0.6 % |
Mangan | 2 % Show Supplier Material materials with Mangan of 2 % |
Molybdän | 0.1 - 0.6 % Show Supplier Material materials with Molybdän of 0.1 - 0.6 % |
Nickel | 3.5 - 5.5 % Show Supplier Material materials with Nickel of 3.5 - 5.5 % |
Phosphor | 0.04 % Show Supplier Material materials with Phosphor of 0.04 % |
Schwefel | 0.015 % Show Supplier Material materials with Schwefel of 0.015 % |
Silizium | 1 % Show Supplier Material materials with Silizium of 1 % |
Stickstoff | 0.05 - 0.2 % Show Supplier Material materials with Stickstoff of 0.05 - 0.2 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The main applications are for details with special requirements for high corrosion resistance. | |
| Corrosion properties | Good resistance to stress corrosion cracking, Good resistance to pitting and crevice corrosion, High resistance to general corrosion, High resistance to erosion corrosion and corrosion fatigue. PREN ≥ 28 | |
| Heat Treatment | Solution annealing at 1020 – 1100°C followed by water quenching | |
| Welding | Very good | |