Eigenschaften
Allgemein
| Property | Value | Comment |
|---|---|---|
Dichte | 1.24 - 1.25 g/cm³ Show Supplier Material materials with Dichte of 1.24 - 1.25 g/cm³ | ISO 1183 (Maximum value is reached through annealing) |
Abmessung
Mechanisch
| Property | Value | Comment |
|---|---|---|
Biegefestigkeit | 90.0 - 93.0 MPa Show Supplier Material materials with Biegefestigkeit of 90.0 - 93.0 MPa | ISO 178(Maximum value is reached through annealing) |
Biegemodul | 3.43 GPa Show Supplier Material materials with Biegemodul of 3.43 GPa | ISO 178(Maximum value is reached through annealing) |
3.435 GPa Show Supplier Material materials with Biegemodul of 3.435 GPa | ISO 178(Maximum value is reached through annealing) | |
Dehnung | 2.4 - 2.7 % Show Supplier Material materials with Dehnung of 2.4 - 2.7 % | ISO 178(Minimum value is reached through annealing) |
Elastizitätsmodul | 3.65 - 3.71 GPa Show Supplier Material materials with Elastizitätsmodul of 3.65 - 3.71 GPa | ISO 527 (Maximum value is reached through annealing) |
Schlagzähigkeit, Charpy ungekerbt | 11 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 11 kJ/m² | ISO 179-1 (Maximum value is reached through annealing) |
20 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179-1 (Maximum value is reached through annealing) | |
Zugfestigkeit | 45.0 - 51.0 MPa Show Supplier Material materials with Zugfestigkeit of 45.0 - 51.0 MPa | ISO 527 (Maximum value is reached through annealing) |
Thermisch
| Property | Value | Pressure | Comment |
|---|---|---|---|
Wärmeformbeständigkeitstemperatur | 80 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 80 °C | 1.8 MPa | ISO 75, unannealed-annealed condition |
144 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 144 °C | 1.8 MPa | ISO 75, unannealed-annealed condition |
Technological properties
| Property | ||
|---|---|---|
| Application areas | TOYS OR THEIR ELEMENTS: human figures, animals, constructions, houses, vehicles, dice - GADGETS OR THEIR ELEMENTS: key rings, stands, phone cases - PROTOTYPES: tools, concept models - ELEMENTS OF JEWELLERY: earrings, bracelets, beads, necklaces - SPARE PARTS: elements of machines, equipment, vehicles, electronic equipment - TOOLS: complex elements requiring durability - HOUSE EQUIPMENT: bowls, trays, boxes | |
| Processing methods | Print temperature: 200-230°C, Bed temperature: 50-70°C (when using plates or other means to increase the adhesion, the heating of the bed is not required) - heating of the print should be conducted in accordance with the manual provided by Fiberlogy | |