Property | Value |
---|---|
Dichte | 9.13 g/cm³ Show Supplier Material materials with Dichte of 9.13 g/cm³ |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 30 % Show Supplier Material materials with Dehnung of 30 % | ||
Elastizitätsmodul | 20 °C | 225 GPa Show Supplier Material materials with Elastizitätsmodul of 225 GPa | |
250 °C | 214 GPa Show Supplier Material materials with Elastizitätsmodul of 214 GPa | ||
500 °C | 188 GPa Show Supplier Material materials with Elastizitätsmodul of 188 GPa | ||
Zugfestigkeit | 860 MPa Show Supplier Material materials with Zugfestigkeit of 860 MPa | min. |
Thermisch
Property | Value | Comment |
---|---|---|
Koeffizient der thermischen Ausdehnung | 0.0000123 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.0000123 1/K | 20 to 100°C |
Schmelzpunkt | 1330.0 - 1410.0 °C Show Supplier Material materials with Schmelzpunkt of 1330.0 - 1410.0 °C | |
Wärmeleitfähigkeit | 9.4 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 9.4 W/(m·K) |
Elektrisch
Property | Value |
---|---|
spezifischer Widerstand | 8.800000000000001e-10 Ω·m Show Supplier Material materials with spezifischer Widerstand of 8.800000000000001e-10 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Chrom | 19.0 - 21.0 % Show Supplier Material materials with Chrom of 19.0 - 21.0 % | |
Eisen | 3.0 Show Supplier Material materials with Eisen of 3.0 | max. |
Kohlenstoff | 0.05 - 0.15 % Show Supplier Material materials with Kohlenstoff of 0.05 - 0.15 % | |
Mangan | 1.0 - 2.0 % Show Supplier Material materials with Mangan of 1.0 - 2.0 % | |
Nickel | 9.0 - 11.0 % Show Supplier Material materials with Nickel of 9.0 - 11.0 % | |
Phosphor | 0.04 Show Supplier Material materials with Phosphor of 0.04 | max. |
Schwefel | 0.03 Show Supplier Material materials with Schwefel of 0.03 | max. |
Silizium | 0.4 Show Supplier Material materials with Silizium of 0.4 | max. |
Wolfram | 14.0 - 16.0 % Show Supplier Material materials with Wolfram of 14.0 - 16.0 % |
Technological properties
Property | ||
---|---|---|
Application areas | ||
Corrosion properties | UGI® HT605 has excellent corrosion resistance at the high temperatures found in aircraft engines. Resistance to oxidation is good when maintained intermittently at up to 870°C and continuously at up to 1090°C. This grade is highly-resistant to flaking and oxidation under extreme conditions. | |
General machinability | HT605 alloy is machinable using conventional techniques. However, we recommend high-speed steel tools (M40 type) or carbide tools (C1, C2 or C3 type) used on rigid equipment. HT605 alloy is more difficult to machine than austenitic stainless steels (302, 304, 321, and 347 types). Generally, we suggest reducing the feed rates, cutting speeds and pass depths. Please contact our technical assistance team for further information. | |
Other | Available products: Others on demand. |