DIN 1725-1 Grade 3.2315 T8

Want to keep this datasheet? Save it now in your required format

Description

From the type of alloy AlMgSi is the alloy AlMgSi1 that, which used longest. This cold and/or hot hardenable material reaches strength values of 200 to 315 MPa with A5-elongation at break of approx. 6 to 18 %. In hot and cold-hardened condition is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodising of this material are good. Although this alloy achieves the highest mechanical strength of all alloys of this type, it is used with priority due to its good corrosion resistance. Furthermore it, although the weldability is good, is used more for screwing and/or rivet joints, because within the welding seam range there is the danger of destabilizations. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperature hot ageing: 4 to 16 h at 155 to 190 °C Application: For bearing constructions (loadedstatically according to DIN 4113), in the apparatus and tank construction for heat exchangers, for compressed gas bottles, technical flow pressed parts, in the automobile engineering for tank and silo trucks, for dump truck hollows, buses, body parts, for safety-related parts, wheels and superstructures. In mechanical engineering for devices, tools (baseplates, head and stamp retaining plates as well as guide plates), machine tables, hydraulic/pneumatics, shaft couplings (forging), roller pipes, brake disks and brake drums (with squirted wear course), liaison vehicles (screws according to DIN 267 T18, rivets), in food industry (including commercial devices), in the building of rail-mounted vehicles for railroad car doors, stroke sun roofs, wheel-center disks, axle box case, car boxes, in shipbuilding for the trunk, for superstructures, sail masts, equipment for radar, in the mining industry, in the building industry for rolling shutter, roll gates, for camping furniture and for metal goods (building fittings, table-ware, reflectors etc.).

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Empfohlene Literatur

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Alle anzeigen

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte	20.0 °C	2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dehnung	20.0 °C	3.0 % Show Material materials with Dehnung of 3.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Wire	A100
	20.0 °C	6.0 % Show Material materials with Dehnung of 6.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Rod
	20.0 °C	7.0 % Show Material materials with Dehnung of 7.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Wire	A10
	20.0 °C	8.0 % Show Material materials with Dehnung of 8.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Strip, Tube	A10
	20.0 °C	8.0 % Show Material materials with Dehnung of 8.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Rod, Sheet
	20.0 °C	9.0 % Show Material materials with Dehnung of 9.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Sheet
	20.0 °C	10.0 % Show Material materials with Dehnung of 10.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Tube	A10
	20.0 °C	10.0 % Show Material materials with Dehnung of 10.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Strip, Tube
	20.0 °C	12.0 % Show Material materials with Dehnung of 12.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Flat	A10
	20.0 °C	12.0 % Show Material materials with Dehnung of 12.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Tube
	20.0 °C	14.0 % Show Material materials with Dehnung of 14.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Flat
Elastizitätsmodul	20.0 °C	68.0 - 73.0 GPa Show Material materials with Elastizitätsmodul of 68.0 - 73.0 GPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Härte, Brinell	20.0 °C	80.0 [-] Show Material materials with Härte, Brinell of 80.0 [-]	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Tube
	20.0 °C	85.0 [-] Show Material materials with Härte, Brinell of 85.0 [-]	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Sheet, Flat
	20.0 °C	90.0 - 95.0 [-] Show Material materials with Härte, Brinell of 90.0 - 95.0 [-]	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Sheet
	20.0 °C	90.0 [-] Show Material materials with Härte, Brinell of 90.0 [-]	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Sheet
	20.0 °C	95.0 [-] Show Material materials with Härte, Brinell of 95.0 [-]	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Strip, Tube, Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Schubmodule	20.0 °C	26.0 - 27.0 GPa Show Material materials with Schubmodule of 26.0 - 27.0 GPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Zugfestigkeit	20.0 °C	270.0 MPa Show Material materials with Zugfestigkeit of 270.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Rod
	20.0 °C	275.0 MPa Show Material materials with Zugfestigkeit of 275.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Tube
	20.0 °C	295.0 MPa Show Material materials with Zugfestigkeit of 295.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Sheet
	20.0 °C	300.0 MPa Show Material materials with Zugfestigkeit of 300.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Rod
	20.0 °C	310.0 MPa Show Material materials with Zugfestigkeit of 310.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Tube
	20.0 °C	315.0 MPa Show Material materials with Zugfestigkeit of 315.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Sheet, Strip
	20.0 °C	320.0 MPa Show Material materials with Zugfestigkeit of 320.0 MPa	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Wire

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Koeffizient der thermischen Ausdehnung		1.6e-05 - 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 - 2.4e-05 1/K				Typical for Wrought 6000 Series Aluminium
Schmelzpunkt		555.0 - 655.0 °C Show Material materials with Schmelzpunkt of 555.0 - 655.0 °C				Typical for Wrought 6000 Series Aluminium
Spezifische Wärmekapazität		887.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 887.0 - 963.0 J/(kg·K)				Typical for Wrought 6000 Series Aluminium
Wärmeleitfähigkeit	20.0 °C	170.0 - 220.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 170.0 - 220.0 W/(m·K)	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire

Elektrisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elektrische Leitfähigkeit	20.0 °C	24000000.0 - 32000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 - 32000000.0 S/m	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
spezifischer Widerstand		2.9e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.9e-08 - 5e-08 Ω·m				Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chrom	0.25 Show Material materials with Chrom of 0.25	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Eisen	0.5 Show Material materials with Eisen of 0.5	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Kupfer	0.1 Show Material materials with Kupfer of 0.1	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Magnesium	0.6 - 1.2 % Show Material materials with Magnesium of 0.6 - 1.2 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Mangan	0.4 - 1.0 % Show Material materials with Mangan of 0.4 - 1.0 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Silizium	0.7 - 1.3 % Show Material materials with Silizium of 0.7 - 1.3 %	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Titan	0.1 Show Material materials with Titan of 0.1	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire
Zink	0.2 Show Material materials with Zink of 0.2	T8	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 240, VdTÜV WB 414, VdTÜV WB 327, VdTÜV WB 423, VdTÜV WB 493	Profile, Rod, Sheet, Flat, Strip, Tube, Wire

Technological properties

Property

Workability

Excellent workability.

Looking for suppliers of this material? Click to see 10 supplier of DIN 1725-1 Grade 3.2315 T8 on Matmatch