WL 3.1924-1 Grade 3.1924 T652

Want to keep this datasheet? Save it now in your required format

Description

Alloy AlCu2MgNi (AlCuMgFeNi) is an especially for aircraft construction modified alloy of type AlCuMg. Beside 2,5 % Cu it contains 1,5 % Mg as well as 1,1 % Fe and Ni. It is a natural and artificial ageable, high-strength alloy and achieves tensile strength values up to 430MPa at A5-ductile yiled of 3 to 8%. Heat-resistance properties of this alloy are enhancable by Fe- and Ni-content what represents the dominating application attribute. Heat-treatment instructions have to be most accurately adhered in order to warrant high heat-strength up to 250 deg. C. Usual semi-finished forms are thick plates, rods as well as die and free-form forged parts. This material has a high machinability, anodizability and hot-workability. It is cold-workable in soft condition resp. 2 h after solution annealing only. The alloy is not suitable for welding. Its corrosion resistance is satisfactory only. Application: in aircraft construction for large structure and power plant parts.

Related Standards

WL 3.1924-1

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Empfohlene Literatur

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Alle anzeigen

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Eigenschaften

Allgemein

Property	Value	Comment
Dichte	2.75 - 2.84 g/cm³ Show Material materials with Dichte of 2.75 - 2.84 g/cm³	Typical for Wrought 2000 Series Aluminium

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastizitätsmodul		70.0 - 73.0 GPa Show Material materials with Elastizitätsmodul of 70.0 - 73.0 GPa				Typical for Wrought 2000 Series Aluminium
Härte, Brinell	20.0 °C	125.0 [-] Show Material materials with Härte, Brinell of 125.0 [-]	T652	WL 3.1924-1	Forging	Transverse
	20.0 °C	125.0 [-] Show Material materials with Härte, Brinell of 125.0 [-]	T652	WL 3.1924-1	Forging
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 2000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 2000 Series Aluminium
Schubmodule		26.0 - 27.5 GPa Show Material materials with Schubmodule of 26.0 - 27.5 GPa				Typical for Wrought 2000 Series Aluminium
Zugfestigkeit	20.0 °C	380.0 MPa Show Material materials with Zugfestigkeit of 380.0 MPa	T652	WL 3.1924-1	Forging	Transverse
	20.0 °C	390.0 MPa Show Material materials with Zugfestigkeit of 390.0 MPa	T652	WL 3.1924-1	Forging	Transverse
	20.0 °C	400.0 MPa Show Material materials with Zugfestigkeit of 400.0 MPa	T652	WL 3.1924-1	Forging
	20.0 °C	410.0 MPa Show Material materials with Zugfestigkeit of 410.0 MPa	T652	WL 3.1924-1	Forging	Transverse
	20.0 °C	420.0 MPa Show Material materials with Zugfestigkeit of 420.0 MPa	T652	WL 3.1924-1	Forging

Thermisch

Property	Value	Comment
Koeffizient der thermischen Ausdehnung	1.6e-05 - 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 - 2.4e-05 1/K	Typical for Wrought 2000 Series Aluminium
Schmelzpunkt	500.0 - 650.0 °C Show Material materials with Schmelzpunkt of 500.0 - 650.0 °C	Typical for Wrought 2000 Series Aluminium
Spezifische Wärmekapazität	816.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 816.0 - 963.0 J/(kg·K)	Typical for Wrought 2000 Series Aluminium
Wärmeleitfähigkeit	112.0 - 251.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 112.0 - 251.0 W/(m·K)	Typical for Wrought 2000 Series Aluminium

Elektrisch

Property	Value	Comment
Elektrische Leitfähigkeit	18000000.0 - 30000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 - 30000000.0 S/m	Typical for Wrought 2000 Series Aluminium
spezifischer Widerstand	3.4e-08 - 6e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.4e-08 - 6e-08 Ω·m	Typical for Wrought 2000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Eisen	0.9 - 1.4 % Show Material materials with Eisen of 0.9 - 1.4 %	T652	WL 3.1924-1	Forging
Kupfer	1.8 - 2.7 % Show Material materials with Kupfer of 1.8 - 2.7 %	T652	WL 3.1924-1	Forging
Magnesium	1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 %	T652	WL 3.1924-1	Forging
Mangan	0.2 Show Material materials with Mangan of 0.2	T652	WL 3.1924-1	Forging
Nickel	0.8 - 1.4 % Show Material materials with Nickel of 0.8 - 1.4 %	T652	WL 3.1924-1	Forging
Silizium	0.15 - 0.25 % Show Material materials with Silizium of 0.15 - 0.25 %	T652	WL 3.1924-1	Forging
Titan	0.2 Show Material materials with Titan of 0.2	T652	WL 3.1924-1	Forging
Zink	0.1 Show Material materials with Zink of 0.1	T652	WL 3.1924-1	Forging

Technological properties

Property

Workability

Moderate Workability

Looking for suppliers of this material? Click to see 3 supplier of WL 3.1924-1 Grade 3.1924 T652 on Matmatch