General
Property | Value | Condition | Related Standards |
---|---|---|---|
Densidad | 2.82 g/cm³ Show Material materials with Densidad of 2.82 g/cm³ | T61 | AA Standards, ASTM B247 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 115.0 MPa Show Material materials with Bending Fatigue Strength of 115.0 MPa | T61 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Dureza Brinell | 120.0 [-] Show Material materials with Dureza Brinell of 120.0 [-] | T61 | AA Standards | |
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Módulo elástico | 74.0 GPa Show Material materials with Módulo elástico of 74.0 GPa | T61 | AA Standards, ASTM B247 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 380.0 MPa Show Material materials with Resistencia a la tracción of 380.0 MPa | T61 | AA Standards, ASTM B247 | |
420.0 MPa Show Material materials with Resistencia a la tracción of 420.0 MPa | T61 | AA Standards |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 816.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | T61 | AA Standards, ASTM B247 | |
100 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | T61 | AA Standards, ASTM B247 | ||
Conductividad térmica | 155 W/(m·K) Show Material materials with Conductividad térmica of 155 W/(m·K) | T61 | AA Standards, ASTM B247 | ||
Temperatura de fusión | 505.0 - 640.0 °C Show Material materials with Temperatura de fusión of 505.0 - 640.0 °C | T61 | AA Standards, ASTM B247 |
Eléctrico
Property | Value | Condition | Related Standards |
---|---|---|---|
Conductividad eléctrica | 23000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 S/m | T61 | AA Standards, ASTM B247 |
Resistividad eléctrica | 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.35e-08 Ω·m | T61 | AA Standards, ASTM B247 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Cobre | 3.5 - 4.5 % Show Material materials with Cobre of 3.5 - 4.5 % | T61 | AA Standards, ASTM B247 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T61 | AA Standards, ASTM B247 |
Hierro | 1.00 % Show Material materials with Hierro of 1.00 % | T61 | AA Standards, ASTM B247 |
Magnesio | 0.45 - 0.9 % Show Material materials with Magnesio of 0.45 - 0.9 % | T61 | AA Standards, ASTM B247 |
Manganeso | 0.2 % Show Material materials with Manganeso of 0.2 % | T61 | AA Standards, ASTM B247 |
Níquel | 1.7 - 2.3 % Show Material materials with Níquel of 1.7 - 2.3 % | T61 | AA Standards, ASTM B247 |
Silicona | 0.9 % Show Material materials with Silicona of 0.9 % | T61 | AA Standards, ASTM B247 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T61 | AA Standards, ASTM B247 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
General machinability | General: good to acceptable | |
Workability | Moderate Workability |