Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.75 g/cm³ Show Material materials with Densidad of 2.75 g/cm³ | T4 | AA Standards, ASTM B316 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | T4 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Dureza Brinell | 70.0 [-] Show Material materials with Dureza Brinell of 70.0 [-] | T4 | AA Standards | |
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | T4 | AA Standards, ASTM B316 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | T4 | AA Standards, ASTM B316 | |
295.0 MPa Show Material materials with Resistencia a la tracción of 295.0 MPa | T4 | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 816.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | T4 | AA Standards, ASTM B316 | |
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | T4 | AA Standards, ASTM B316 | ||
Conductividad térmica | 155 W/(m·K) Show Material materials with Conductividad térmica of 155 W/(m·K) | T4 | AA Standards, ASTM B316 | ||
Temperatura de fusión | 550.0 - 650.0 °C Show Material materials with Temperatura de fusión of 550.0 - 650.0 °C | T4 | AA Standards, ASTM B316 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 23000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 S/m | T4 | AA Standards, ASTM B316 |
Resistividad eléctrica | 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.35e-08 Ω·m | T4 | AA Standards, ASTM B316 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 2.2 - 3.0 % Show Material materials with Cobre of 2.2 - 3.0 % | T4 | AA Standards, ASTM B316 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T4 | AA Standards, ASTM B316 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T4 | AA Standards, ASTM B316 |
Magnesio | 0.2 - 0.5 % Show Material materials with Magnesio of 0.2 - 0.5 % | T4 | AA Standards, ASTM B316 |
Manganeso | 0.2 % Show Material materials with Manganeso of 0.2 % | T4 | AA Standards, ASTM B316 |
Silicona | 0.8 % Show Material materials with Silicona of 0.8 % | T4 | AA Standards, ASTM B316 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T4 | AA Standards, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: acceptable, in principle it should be protected | |
| General machinability | General: sufficient | |
| Workability | general (condition): acceptable | |