Propiedades
General
| Property | Value | Comment |
|---|---|---|
Densidad | 2.75 - 2.84 g/cm³ Show Material materials with Densidad of 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | T61 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Dureza Brinell | 115.0 [-] Show Material materials with Dureza Brinell of 115.0 [-] | T61 | AA Standards | |
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Módulo elástico | 70.0 - 73.0 GPa Show Material materials with Módulo elástico of 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 350.0 MPa Show Material materials with Resistencia a la tracción of 350.0 MPa | T61 | AA Standards, ASTM B247 | |
360.0 MPa Show Material materials with Resistencia a la tracción of 360.0 MPa | T61 | AA Standards, ASTM B247 | ||
365.0 MPa Show Material materials with Resistencia a la tracción of 365.0 MPa | T61 | AA Standards, ASTM B247 | ||
380.0 MPa Show Material materials with Resistencia a la tracción of 380.0 MPa | T61 | AA Standards, ASTM B247 | ||
385.0 MPa Show Material materials with Resistencia a la tracción of 385.0 MPa | T61 | AA Standards, ASTM B247 | ||
395.0 MPa Show Material materials with Resistencia a la tracción of 395.0 MPa | T61 | AA Standards, ASTM B247 | ||
400.0 MPa Show Material materials with Resistencia a la tracción of 400.0 MPa | T61 | AA Standards, ASTM B247 | ||
440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | T61 | AA Standards |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Calor específico | 816.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Coeficiente de dilatación térmica | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Conductividad térmica | 112.0 - 251.0 W/(m·K) Show Material materials with Conductividad térmica of 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Temperatura de fusión | 500.0 - 650.0 °C Show Material materials with Temperatura de fusión of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Eléctrico
| Property | Value | Comment |
|---|---|---|
Conductividad eléctrica | 18000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Resistividad eléctrica | 3.4e-08 - 6e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 1.9 - 2.7 % Show Material materials with Cobre of 1.9 - 2.7 % | T61 | AA Standards, ASTM B247 |
Hierro | 0.9 - 1.3 % Show Material materials with Hierro of 0.9 - 1.3 % | T61 | AA Standards, ASTM B247 |
Magnesio | 1.3 - 1.8 % Show Material materials with Magnesio of 1.3 - 1.8 % | T61 | AA Standards, ASTM B247 |
Níquel | 0.9 - 1.2 % Show Material materials with Níquel of 0.9 - 1.2 % | T61 | AA Standards, ASTM B247 |
Silicona | 0.1 - 0.25 % Show Material materials with Silicona of 0.1 - 0.25 % | T61 | AA Standards, ASTM B247 |
Titanio | 0.04 - 0.1 % Show Material materials with Titanio of 0.04 - 0.1 % | T61 | AA Standards, ASTM B247 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T61 | AA Standards, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | Moderate Workability | |