Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ | T6 | AA Standards, ASTM B247 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | T6 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 4000 Series Aluminium | ||
Dureza Brinell | 120.0 [-] Show Material materials with Dureza Brinell of 120.0 [-] | T6 | AA Standards | |
Módulo de cizallamiento | 26.0 GPa Show Material materials with Módulo de cizallamiento of 26.0 GPa | Typical for Wrought 4000 Series Aluminium | ||
Módulo elástico | 79.0 GPa Show Material materials with Módulo elástico of 79.0 GPa | T6 | AA Standards, ASTM B247 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 4000 Series Aluminium | ||
Resistencia a la tracción | 360.0 MPa Show Material materials with Resistencia a la tracción of 360.0 MPa | T6 | AA Standards, ASTM B247 | |
380.0 MPa Show Material materials with Resistencia a la tracción of 380.0 MPa | T6 | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 864.0 J/(kg·K) Show Material materials with Calor específico of 864.0 J/(kg·K) | Typical for Wrought 4000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 1.9399999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.9399999999999997e-05 1/K | T6 | AA Standards, ASTM B247 | |
100 °C | 1.9399999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.9399999999999997e-05 1/K | T6 | AA Standards, ASTM B247 | ||
Conductividad térmica | 138.0 - 155.0 W/(m·K) Show Material materials with Conductividad térmica of 138.0 - 155.0 W/(m·K) | T6 | AA Standards, ASTM B247 | ||
Temperatura de fusión | 530.0 - 570.0 °C Show Material materials with Temperatura de fusión of 530.0 - 570.0 °C | T6 | AA Standards, ASTM B247 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 20000000.0 - 23000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 - 23000000.0 S/m | T6 | AA Standards, ASTM B247 |
Resistividad eléctrica | 4.35e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.35e-08 - 5e-08 Ω·m | T6 | AA Standards, ASTM B247 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 0.5 - 1.3 % Show Material materials with Cobre of 0.5 - 1.3 % | T6 | AA Standards, ASTM B247 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T6 | AA Standards, ASTM B247 |
Hierro | 1.00 % Show Material materials with Hierro of 1.00 % | T6 | AA Standards, ASTM B247 |
Magnesio | 0.8 - 1.3 % Show Material materials with Magnesio of 0.8 - 1.3 % | T6 | AA Standards, ASTM B247 |
Níquel | 0.5 - 1.3 % Show Material materials with Níquel of 0.5 - 1.3 % | T6 | AA Standards, ASTM B247 |
Silicona | 11.0 - 13.5 % Show Material materials with Silicona of 11.0 - 13.5 % | T6 | AA Standards, ASTM B247 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T6 | AA Standards, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation, limited damage during laboratory tests, general: acceptable, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | Moderate Workability | |