General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.66 g/cm³ Show Material materials with Densidad of 2.66 g/cm³ | H112 | AA Standards, ASTM B209 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 115.0 MPa Show Material materials with Bending Fatigue Strength of 115.0 MPa | H112 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Dureza Brinell | 63.0 [-] Show Material materials with Dureza Brinell of 63.0 [-] | H112 | AA Standards | |
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | H112 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 205.0 MPa Show Material materials with Resistencia a la tracción of 205.0 MPa | H112 | AA Standards, ASTM B209 | |
210.0 MPa Show Material materials with Resistencia a la tracción of 210.0 MPa | H112 | AA Standards, ASTM B209 | ||
220.0 MPa Show Material materials with Resistencia a la tracción of 220.0 MPa | H112 | AA Standards, ASTM B209 | ||
240.0 MPa Show Material materials with Resistencia a la tracción of 240.0 MPa | H112 | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 879.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | H112 | AA Standards, ASTM B209 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | H112 | AA Standards, ASTM B209 | ||
Conductividad térmica | 126 W/(m·K) Show Material materials with Conductividad térmica of 126 W/(m·K) | H112 | AA Standards, ASTM B209 | ||
Temperatura de fusión | 590.0 - 645.0 °C Show Material materials with Temperatura de fusión of 590.0 - 645.0 °C | H112 | AA Standards, ASTM B209 | ||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 19000000.0 S/m Show Material materials with Conductividad eléctrica of 19000000.0 S/m | H112 | AA Standards, ASTM B209 |
Resistividad eléctrica | 5.26e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.26e-08 Ω·m | H112 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 0.05 % Show Material materials with Cobre of 0.05 % | H112 | AA Standards, ASTM B209 |
Cromo | 0.15 - 0.35 % Show Material materials with Cromo of 0.15 - 0.35 % | H112 | AA Standards, ASTM B209 |
Magnesio | 3.1 - 3.9 % Show Material materials with Magnesio of 3.1 - 3.9 % | H112 | AA Standards, ASTM B209 |
Manganeso | 0.01 % Show Material materials with Manganeso of 0.01 % | H112 | AA Standards, ASTM B209 |
Titanio | 0.05 % Show Material materials with Titanio of 0.05 % | H112 | AA Standards, ASTM B209 |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H112 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |