General
Property | Value | Condition | Related Standards |
---|---|---|---|
Densidad | 2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³ | H28 | AA Standards, ASTM B209 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Dureza Brinell | 50.0 [-] Show Material materials with Dureza Brinell of 50.0 [-] | H28 | AA Standards | |
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H28 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa | H28 | AA Standards, ASTM B209 | |
195.0 MPa Show Material materials with Resistencia a la tracción of 195.0 MPa | H28 | AA Standards |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 879.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | H28 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | H28 | AA Standards, ASTM B209 | ||
Conductividad térmica | 205 W/(m·K) Show Material materials with Conductividad térmica of 205 W/(m·K) | H28 | AA Standards, ASTM B209 | ||
Temperatura de fusión | 635.0 - 655.0 °C Show Material materials with Temperatura de fusión of 635.0 - 655.0 °C | H28 | AA Standards, ASTM B209 | ||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
Property | Value | Condition | Related Standards |
---|---|---|---|
Conductividad eléctrica | 31000000.0 S/m Show Material materials with Conductividad eléctrica of 31000000.0 S/m | H28 | AA Standards, ASTM B209 |
Resistividad eléctrica | 3.23e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.23e-08 Ω·m | H28 | AA Standards, ASTM B209 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H28 | AA Standards, ASTM B209 |
Galio | 0.03 % Show Material materials with Galio of 0.03 % | H28 | AA Standards, ASTM B209 |
Hierro | 0.10 % Show Material materials with Hierro of 0.10 % | H28 | AA Standards, ASTM B209 |
Magnesio | 0.6 - 1.0 % Show Material materials with Magnesio of 0.6 - 1.0 % | H28 | AA Standards, ASTM B209 |
Manganeso | 0.03 % Show Material materials with Manganeso of 0.03 % | H28 | AA Standards, ASTM B209 |
Silicona | 0.08 % Show Material materials with Silicona of 0.08 % | H28 | AA Standards, ASTM B209 |
Vanadio | 0.05 % Show Material materials with Vanadio of 0.05 % | H28 | AA Standards, ASTM B209 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | H28 | AA Standards, ASTM B209 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (H241, H25, H26, H28) | |
Workability | general (condition): good (H241), acceptable (H25, H26), poor(H28) |