Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | T61 | AA Standards, ASTM B317 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | T61 | AA Standards, ASTM B317 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Resistencia a la tracción | 105.0 MPa Show Material materials with Resistencia a la tracción of 105.0 MPa | T61 | AA Standards, ASTM B317 | |
125.0 MPa Show Material materials with Resistencia a la tracción of 125.0 MPa | T61 | AA Standards, ASTM B317 | ||
140.0 MPa Show Material materials with Resistencia a la tracción of 140.0 MPa | T61 | AA Standards, ASTM B317 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T61 | AA Standards, ASTM B317 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T61 | AA Standards, ASTM B317 | ||
Conductividad térmica | 218.0 - 226.0 W/(m·K) Show Material materials with Conductividad térmica of 218.0 - 226.0 W/(m·K) | T61 | AA Standards, ASTM B317 | ||
Temperatura de fusión | 620.0 - 655.0 °C Show Material materials with Temperatura de fusión of 620.0 - 655.0 °C | T61 | AA Standards, ASTM B317 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 33000000.0 - 35000000.0 S/m Show Material materials with Conductividad eléctrica of 33000000.0 - 35000000.0 S/m | T61 | AA Standards, ASTM B317 |
Resistividad eléctrica | 2.86e-08 - 3.03e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.86e-08 - 3.03e-08 Ω·m | T61 | AA Standards, ASTM B317 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Boro | 0.06 % Show Material materials with Boro of 0.06 % | T61 | AA Standards, ASTM B317 |
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | T61 | AA Standards, ASTM B317 |
Cromo | 0.03 % Show Material materials with Cromo of 0.03 % | T61 | AA Standards, ASTM B317 |
Hierro | 0.50 % Show Material materials with Hierro of 0.50 % | T61 | AA Standards, ASTM B317 |
Magnesio | 0.35 - 0.8 % Show Material materials with Magnesio of 0.35 - 0.8 % | T61 | AA Standards, ASTM B317 |
Manganeso | 0.03 % Show Material materials with Manganeso of 0.03 % | T61 | AA Standards, ASTM B317 |
Silicona | 0.3 - 0.7 % Show Material materials with Silicona of 0.3 - 0.7 % | T61 | AA Standards, ASTM B317 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T61 | AA Standards, ASTM B317 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: sufficient (T6, T63), poor (T61, T64) | |
| Workability | general (condition): poor(T6, T63), acceptable (T61, T64) | |