Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³ | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | T9 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Dureza Brinell | 120.0 [-] Show Material materials with Dureza Brinell of 120.0 [-] | T9 | AA Standards | |
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Resistencia a la tracción | 330.0 MPa Show Material materials with Resistencia a la tracción of 330.0 MPa | T9 | AA Standards, ASTM B210, ASTM B483 | |
345.0 MPa Show Material materials with Resistencia a la tracción of 345.0 MPa | T9 | AA Standards, ASTM B211 | ||
360.0 MPa Show Material materials with Resistencia a la tracción of 360.0 MPa | T9 | AA Standards, ASTM B211 | ||
400.0 MPa Show Material materials with Resistencia a la tracción of 400.0 MPa | T9 | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | ||
Conductividad térmica | 172 W/(m·K) Show Material materials with Conductividad térmica of 172 W/(m·K) | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | ||
Temperatura de fusión | 580.0 - 650.0 °C Show Material materials with Temperatura de fusión of 580.0 - 650.0 °C | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 26000000.0 S/m Show Material materials with Conductividad eléctrica of 26000000.0 S/m | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Resistividad eléctrica | 3.85e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 Ω·m | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuto | 0.4 - 0.7 % Show Material materials with Bismuto of 0.4 - 0.7 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Cobre | 0.15 - 0.4 % Show Material materials with Cobre of 0.15 - 0.4 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Cromo | 0.04 - 0.14 % Show Material materials with Cromo of 0.04 - 0.14 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Magnesio | 0.8 - 1.2 % Show Material materials with Magnesio of 0.8 - 1.2 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Manganeso | 0.15 % Show Material materials with Manganeso of 0.15 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Plomo | 0.4 - 0.7 % Show Material materials with Plomo of 0.4 - 0.7 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Silicona | 0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: good to acceptable (T6, T651, T6510, T6511, T9) | |
| Workability | general (condition): poor(T6, T651, T6510, T6511), not suitable (T9) | |