Propiedades
General
| Property | Value | Comment |
|---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | Typical for Wrought 6000 Series Aluminium |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Resistencia a la tracción | 260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | T6510 | AA Standards, ASTM B221 |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Calor específico | 887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Coeficiente de dilatación térmica | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Conductividad térmica | 170.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Temperatura de fusión | 555.0 - 655.0 °C Show Material materials with Temperatura de fusión of 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Eléctrico
| Property | Value | Comment |
|---|---|---|
Conductividad eléctrica | 21000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Resistividad eléctrica | 2.9e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuto | 0.4 - 0.7 % Show Material materials with Bismuto of 0.4 - 0.7 % | T6510 | AA Standards, ASTM B221 |
Cobre | 0.15 - 0.4 % Show Material materials with Cobre of 0.15 - 0.4 % | T6510 | AA Standards, ASTM B221 |
Cromo | 0.04 - 0.14 % Show Material materials with Cromo of 0.04 - 0.14 % | T6510 | AA Standards, ASTM B221 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T6510 | AA Standards, ASTM B221 |
Magnesio | 0.8 - 1.2 % Show Material materials with Magnesio of 0.8 - 1.2 % | T6510 | AA Standards, ASTM B221 |
Manganeso | 0.15 % Show Material materials with Manganeso of 0.15 % | T6510 | AA Standards, ASTM B221 |
Plomo | 0.4 - 0.7 % Show Material materials with Plomo of 0.4 - 0.7 % | T6510 | AA Standards, ASTM B221 |
Silicona | 0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 % | T6510 | AA Standards, ASTM B221 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T6510 | AA Standards, ASTM B221 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T6510 | AA Standards, ASTM B221 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: good to acceptable (T6, T651, T6510, T6511, T9) | |
| Workability | general (condition): poor(T6, T651, T6510, T6511), not suitable (T9) | |