Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.69 g/cm³ Show Material materials with Densidad of 2.69 g/cm³ | T1 | AA Standards, ASTM B221 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 70.0 MPa Show Material materials with Bending Fatigue Strength of 70.0 MPa | T1 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Dureza Brinell | 42.0 [-] Show Material materials with Dureza Brinell of 42.0 [-] | T1 | AA Standards | |
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | T1 | AA Standards, ASTM B221 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Resistencia a la tracción | 115.0 MPa Show Material materials with Resistencia a la tracción of 115.0 MPa | T1 | AA Standards, ASTM B221 | |
150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | T1 | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T1 | AA Standards, ASTM B221 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T1 | AA Standards, ASTM B221 | ||
Conductividad térmica | 193.0 - 209.0 W/(m·K) Show Material materials with Conductividad térmica of 193.0 - 209.0 W/(m·K) | T1 | AA Standards, ASTM B221 | ||
Temperatura de fusión | 615.0 - 655.0 °C Show Material materials with Temperatura de fusión of 615.0 - 655.0 °C | T1 | AA Standards, ASTM B221 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 29000000.0 - 32000000.0 S/m Show Material materials with Conductividad eléctrica of 29000000.0 - 32000000.0 S/m | T1 | AA Standards, ASTM B221 |
Resistividad eléctrica | 3.13e-08 - 3.45e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.13e-08 - 3.45e-08 Ω·m | T1 | AA Standards, ASTM B221 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 0.2 % Show Material materials with Cobre of 0.2 % | T1 | AA Standards, ASTM B221 |
Hierro | 0.15 % Show Material materials with Hierro of 0.15 % | T1 | AA Standards, ASTM B221 |
Magnesio | 0.45 - 0.9 % Show Material materials with Magnesio of 0.45 - 0.9 % | T1 | AA Standards, ASTM B221 |
Manganeso | 0.05 % Show Material materials with Manganeso of 0.05 % | T1 | AA Standards, ASTM B221 |
Silicona | 0.2 - 0.6 % Show Material materials with Silicona of 0.2 - 0.6 % | T1 | AA Standards, ASTM B221 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | T1 | AA Standards, ASTM B221 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (T1), sufficient (T5, T6) | |
| Workability | general (condition): acceptable (T1, T5), poor(T6) | |