Propiedades
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Densidad | 2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³ | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil | |
20.0 °C | 2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³ | H19 | EN 573-3 | Foil |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 8000 Series Aluminium | ||||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 8000 Series Aluminium | ||||
Resistencia a la tracción | 180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil | ||
20.0 °C | 180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | H19 | EN 573-3 | Foil | ||
20.0 °C | 195.0 MPa Show Material materials with Resistencia a la tracción of 195.0 MPa | H19 | EN 573-3 | Foil |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Calor específico | 920.0 J/(kg·K) Show Material materials with Calor específico of 920.0 J/(kg·K) | Typical for Wrought 8000 Series Aluminium | ||||
Coeficiente de dilatación térmica | 20 °C | 2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil | |
100 °C | 2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil | ||
Conductividad térmica | 20.0 °C | 210.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 210.0 - 220.0 W/(m·K) | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate | |
Temperatura de fusión | 640.0 - 655.0 °C Show Material materials with Temperatura de fusión of 640.0 - 655.0 °C | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil |
Eléctrico
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 34000000.0 - 35000000.0 S/m Show Material materials with Conductividad eléctrica of 34000000.0 - 35000000.0 S/m | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Resistividad eléctrica | 2.86e-08 - 2.94e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.86e-08 - 2.94e-08 Ω·m | H19 | EN 573-3, EN 683 | Strip, Sheet, Plate, Foil |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Hierro | 0.5 - 1.0 % Show Material materials with Hierro of 0.5 - 1.0 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Magnesio | 0.1 % Show Material materials with Magnesio of 0.1 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Silicona | 0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Titanio | 0.05 % Show Material materials with Titanio of 0.05 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H19 | EN 573-3, EN 683 | Foil, Strip, Sheet, Plate |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Corrosion properties | Seawater: sufficient, weathering: acceptable | |
| Workability | Bending / Spinning (cold): good / good, Impact extrusion (cold): good, Deep drawing / upsetting (Condition) good (H14) / good (H14) | |