Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.83 g/cm³ Show Material materials with Densidad of 2.83 g/cm³ | T3 | AA Standards, ASTM B210, ASTM B211 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T3 | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Dureza Brinell | 95.0 [-] Show Material materials with Dureza Brinell of 95.0 [-] | T3 | AA Standards | |
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | T3 | AA Standards, ASTM B210, ASTM B211 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | T3 | AA Standards, ASTM B211 | |
295.0 MPa Show Material materials with Resistencia a la tracción of 295.0 MPa | T3 | AA Standards, ASTM B211 | ||
310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T3 | AA Standards, ASTM B211 | ||
325.0 MPa Show Material materials with Resistencia a la tracción of 325.0 MPa | T3 | AA Standards, ASTM B210 | ||
380.0 MPa Show Material materials with Resistencia a la tracción of 380.0 MPa | T3 | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 816.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.2899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2899999999999998e-05 1/K | T3 | AA Standards, ASTM B210, ASTM B211 | |
100 °C | 2.2899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2899999999999998e-05 1/K | T3 | AA Standards, ASTM B210, ASTM B211 | ||
Conductividad térmica | 151.0 - 172.0 W/(m·K) Show Material materials with Conductividad térmica of 151.0 - 172.0 W/(m·K) | T3 | AA Standards, ASTM B210, ASTM B211 | ||
Temperatura de fusión | 540.0 - 645.0 °C Show Material materials with Temperatura de fusión of 540.0 - 645.0 °C | T3 | AA Standards, ASTM B210, ASTM B211 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 23000000.0 - 26000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 26000000.0 S/m | T3 | AA Standards, ASTM B210, ASTM B211 |
Resistividad eléctrica | 3.85e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 - 4.35e-08 Ω·m | T3 | AA Standards, ASTM B210, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuto | 0.2 - 0.6 % Show Material materials with Bismuto of 0.2 - 0.6 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Cobre | 5.0 - 6.0 % Show Material materials with Cobre of 5.0 - 6.0 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Plomo | 0.2 - 0.6 % Show Material materials with Plomo of 0.2 - 0.6 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Zinc | 0.3 % Show Material materials with Zinc of 0.3 % | T3 | AA Standards, ASTM B210, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Limited operational damage(T3, T4, T451), no damage during operation, limited damage during laboratory tests (T8), general: sufficient, in principle it should be protected | |
| General machinability | General: very good | |
| Workability | general (condition): poor(T3), acceptable (T4, T451), d (T8) | |