General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Densidad | 2.75 g/cm³ Show Material materials with Densidad of 2.75 g/cm³ | F | EN 1706 | |
20.0 °C | 2.75 g/cm³ Show Material materials with Densidad of 2.75 g/cm³ | F | DIN 1725-2, EN 1676, EN 1706 |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 - 90.0 MPa | F | EN 1706 | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Dureza Brinell | 60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-] | F | EN 1706 | ||
75.0 [-] Show Material materials with Dureza Brinell of 75.0 [-] | F | EN 1706 | |||
80.0 [-] Show Material materials with Dureza Brinell of 80.0 [-] | F | EN 1706 | |||
20.0 °C | 60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 65.0 - 90.0 [-] Show Material materials with Dureza Brinell of 65.0 - 90.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 70.0 - 110.0 [-] Show Material materials with Dureza Brinell of 70.0 - 110.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 80.0 - 120.0 [-] Show Material materials with Dureza Brinell of 80.0 - 120.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
Elongación | 0.5 % Show Material materials with Elongación of 0.5 % | F | EN 1706 | A50 | |
1.0 % Show Material materials with Elongación of 1.0 % | F | EN 1706 | A50 | ||
20.0 °C | 0.5 % Show Material materials with Elongación of 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 0.5 - 3.0 % Show Material materials with Elongación of 0.5 - 3.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 0.9 % Show Material materials with Elongación of 0.9 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 1.0 - 3.0 % Show Material materials with Elongación of 1.0 - 3.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
220.0 °C | 3.3 % Show Material materials with Elongación of 3.3 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
280.0 °C | 12.0 % Show Material materials with Elongación of 12.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
300.0 °C | 11.9 % Show Material materials with Elongación of 11.9 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
Módulo de cizallamiento | 2.8 GPa Show Material materials with Módulo de cizallamiento of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Módulo elástico | 75.0 GPa Show Material materials with Módulo elástico of 75.0 GPa | F | EN 1706 | ||
20.0 °C | 75.0 GPa Show Material materials with Módulo elástico of 75.0 GPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
Resistencia a la tracción | 150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | F | EN 1706 | ||
170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa | F | EN 1706 | |||
240.0 MPa Show Material materials with Resistencia a la tracción of 240.0 MPa | F | EN 1706 | |||
20.0 °C | 140.0 MPa Show Material materials with Resistencia a la tracción of 140.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 160.0 MPa Show Material materials with Resistencia a la tracción of 160.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 160.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 160.0 - 200.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 180.0 - 240.0 MPa Show Material materials with Resistencia a la tracción of 180.0 - 240.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 240.0 - 310.0 MPa Show Material materials with Resistencia a la tracción of 240.0 - 310.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 243.0 MPa Show Material materials with Resistencia a la tracción of 243.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
220.0 °C | 149.0 MPa Show Material materials with Resistencia a la tracción of 149.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
280.0 °C | 87.0 MPa Show Material materials with Resistencia a la tracción of 87.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
300.0 °C | 67.0 MPa Show Material materials with Resistencia a la tracción of 67.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
Resistencia al cizallamiento | 20.0 °C | 177.0 MPa Show Material materials with Resistencia al cizallamiento of 177.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Calor específico | 880.0 J/(kg·K) Show Material materials with Calor específico of 880.0 J/(kg·K) | F | EN 1706 | |
20.0 °C | 880.0 J/(kg·K) Show Material materials with Calor específico of 880.0 J/(kg·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Coeficiente de dilatación térmica | 20 °C | 2.1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 |
100 °C | 2.1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
200.0 °C | 2.1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
200 °C | 2.1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
Conductividad térmica | 110.0 - 120.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 120.0 W/(m·K) | F | EN 1706 | |
20.0 °C | 110.0 - 130.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 130.0 W/(m·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Temperatura de fusión | 490.0 - 600.0 °C Show Material materials with Temperatura de fusión of 490.0 - 600.0 °C | F | EN 1706 |
Eléctrico
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Conductividad eléctrica | 13000000.0 - 17000000.0 S/m Show Material materials with Conductividad eléctrica of 13000000.0 - 17000000.0 S/m | F | EN 1706 | |
20.0 °C | 14000000.0 - 18000000.0 S/m Show Material materials with Conductividad eléctrica of 14000000.0 - 18000000.0 S/m | F | DIN 1725-2, EN 1676, EN 1706 | |
Resistividad eléctrica | 5.56e-08 - 7.14e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.56e-08 - 7.14e-08 Ω·m | F | EN 1706 | |
5.88e-08 - 7.69e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.88e-08 - 7.69e-08 Ω·m | F | EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 81.2 % Show Material materials with Aluminio of 81.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
82.1 % Show Material materials with Aluminio of 82.1 % | F | DIN 1725-2, EN 1676, EN 1706 | |
Cobre | 2.0 - 3.5 % Show Material materials with Cobre of 2.0 - 3.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Estaño | 0.1 % Show Material materials with Estaño of 0.1 % | F | DIN 1725-2, EN 1676, EN 1706 |
Hierro | 0.8 % Show Material materials with Hierro of 0.8 % | F | DIN 1725-2, EN 1676, EN 1706 |
0.80 % Show Material materials with Hierro of 0.80 % | F | EN 1706 | |
1.2 % Show Material materials with Hierro of 1.2 % | F | DIN 1725-2, EN 1676, EN 1706 | |
1.20 % Show Material materials with Hierro of 1.20 % | F | EN 1706 | |
Magnesio | 0.1 - 0.5 % Show Material materials with Magnesio of 0.1 - 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Manganeso | 0.1 - 0.5 % Show Material materials with Manganeso of 0.1 - 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Níquel | 0.3 % Show Material materials with Níquel of 0.3 % | F | DIN 1725-2, EN 1676, EN 1706 |
Plomo | 0.2 % Show Material materials with Plomo of 0.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
Silicona | 8.0 - 11.0 % Show Material materials with Silicona of 8.0 - 11.0 % | F | DIN 1725-2, EN 1676, EN 1706 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | F | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 1.2 % Show Material materials with Zinc of 1.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not recommended | |
Corrosion properties | general: not sufficient | |
General machinability | after thermal treatment: good | |
Processing methods | permanent mould casting |