DIN 1725-1 Grade 3.0915 O

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlFeSi is alloyed for increasing the strength increase with Fe and Si. The material belongs to the nature-hard aluminum materials. A strength increase can be achieved only by cold forming. The alloy AlFeSi is very well cold and warm formable and has a good thermal and relatively good electrical conductivity. The material is particularly suitable for deep-drawing. It is well solderable. The material is to be oxidized well anodically, i.e. a shining clean surface develops. It is standardised as sheet metal or strip (DIN 1788 and DIN 1745). Application: for screw-type caps, for menu bowls, for light containers, bottle caps, cover containers and other form packing, for metal goods, like trim, decorated tiles, flexible pipes, various deep-drawing products, for heat exchangers and radiator fins

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683
	20.0 °C	2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 8000 Series Aluminium
Dureza Brinell		25.0 [-] Show Material materials with Dureza Brinell of 25.0 [-]	O	EN 573-3, EN 485
	20.0 °C	25.0 [-] Show Material materials with Dureza Brinell of 25.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Elongación		1.0 % Show Material materials with Elongación of 1.0 %	O	EN 573-3, EN 546		A50
		3.0 % Show Material materials with Elongación of 3.0 %	O	EN 573-3, EN 546		A50
		4.0 % Show Material materials with Elongación of 4.0 %	O	EN 573-3, EN 546		A50
		7.0 % Show Material materials with Elongación of 7.0 %	O	EN 573-3, EN 546		A50
		12.0 % Show Material materials with Elongación of 12.0 %	O	EN 573-3, EN 546, EN 683		A50
		16.0 % Show Material materials with Elongación of 16.0 %	O	EN 573-3, EN 546, EN 683		A50
		19.0 % Show Material materials with Elongación of 19.0 %	O	EN 573-3, EN 1396, EN 485		A50
		20.0 % Show Material materials with Elongación of 20.0 %	O	EN 573-3, EN 683		A50
		21.0 % Show Material materials with Elongación of 21.0 %	O	EN 573-3, EN 1396, EN 485		A50
		24.0 % Show Material materials with Elongación of 24.0 %	O	EN 573-3, EN 1396, EN 485		A50
		25.0 % Show Material materials with Elongación of 25.0 %	O	EN 573-3, EN 485		A50
		30.0 % Show Material materials with Elongación of 30.0 %	O	EN 573-3, EN 485		A50
	20.0 °C	5.0 % Show Material materials with Elongación of 5.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	10.0 % Show Material materials with Elongación of 10.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	15.0 % Show Material materials with Elongación of 15.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	20.0 % Show Material materials with Elongación of 20.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	30.0 % Show Material materials with Elongación of 30.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	35.0 % Show Material materials with Elongación of 35.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 8000 Series Aluminium
Resistencia a la tracción		50.0 - 110.0 MPa Show Material materials with Resistencia a la tracción of 50.0 - 110.0 MPa	O	EN 573-3, EN 546
		55.0 - 115.0 MPa Show Material materials with Resistencia a la tracción of 55.0 - 115.0 MPa	O	EN 573-3, EN 546
		55.0 - 120.0 MPa Show Material materials with Resistencia a la tracción of 55.0 - 120.0 MPa	O	EN 573-3, EN 546
		65.0 - 130.0 MPa Show Material materials with Resistencia a la tracción of 65.0 - 130.0 MPa	O	EN 573-3, EN 546, EN 683
		80.0 - 120.0 MPa Show Material materials with Resistencia a la tracción of 80.0 - 120.0 MPa	O	EN 573-3, EN 1396
		85.0 MPa Show Material materials with Resistencia a la tracción of 85.0 MPa	O	EN 573-3, EN 485
	20.0 °C	75.0 - 110.0 MPa Show Material materials with Resistencia a la tracción of 75.0 - 110.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20.0 °C	75.0 - 115.0 MPa Show Material materials with Resistencia a la tracción of 75.0 - 115.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20.0 °C	80.0 - 110.0 MPa Show Material materials with Resistencia a la tracción of 80.0 - 110.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20.0 °C	80.0 - 115.0 MPa Show Material materials with Resistencia a la tracción of 80.0 - 115.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		920.0 J/(kg·K) Show Material materials with Calor específico of 920.0 J/(kg·K)				Typical for Wrought 8000 Series Aluminium
Coeficiente de dilatación térmica	20 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683
	100 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683
Conductividad térmica	20.0 °C	210.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 210.0 - 220.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat
Temperatura de fusión		640.0 - 655.0 °C Show Material materials with Temperatura de fusión of 640.0 - 655.0 °C	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica	20.0 °C	34000000.0 - 35000000.0 S/m Show Material materials with Conductividad eléctrica of 34000000.0 - 35000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat
Resistividad eléctrica		2.86e-08 - 2.94e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.86e-08 - 2.94e-08 Ω·m	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat
Cromo	0.1 % Show Material materials with Cromo of 0.1 %	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683
Hierro	0.5 - 1.0 % Show Material materials with Hierro of 0.5 - 1.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat
Magnesio	0.1 % Show Material materials with Magnesio of 0.1 %	O	EN 573-3, EN 1396, EN 485, EN 546, EN 683
Manganeso	0.1 % Show Material materials with Manganeso of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat
Silicona	0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat
Titanio	0.05 Show Material materials with Titanio of 0.05	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Zinc	0.1 % Show Material materials with Zinc of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546, EN 683	Flat