DIN 1725-1 Grade 3.0915 H22

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlFeSi is alloyed for increasing the strength increase with Fe and Si. The material belongs to the nature-hard aluminum materials. A strength increase can be achieved only by cold forming. The alloy AlFeSi is very well cold and warm formable and has a good thermal and relatively good electrical conductivity. The material is particularly suitable for deep-drawing. It is well solderable. The material is to be oxidized well anodically, i.e. a shining clean surface develops. It is standardised as sheet metal or strip (DIN 1788 and DIN 1745). Application: for screw-type caps, for menu bowls, for light containers, bottle caps, cover containers and other form packing, for metal goods, like trim, decorated tiles, flexible pipes, various deep-drawing products, for heat exchangers and radiator fins

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683
	20.0 °C	2.71 g/cm³ Show Material materials with Densidad of 2.71 g/cm³	H22	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 8000 Series Aluminium
Dureza Brinell		35.0 [-] Show Material materials with Dureza Brinell of 35.0 [-]	H22	EN 573-3, EN 485
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 8000 Series Aluminium
Resistencia a la tracción		90.0 - 150.0 MPa Show Material materials with Resistencia a la tracción of 90.0 - 150.0 MPa	H22	EN 573-3, EN 546, EN 683
		105.0 - 145.0 MPa Show Material materials with Resistencia a la tracción of 105.0 - 145.0 MPa	H22	EN 573-3, EN 485, EN 541
	20.0 °C	110.0 - 150.0 MPa Show Material materials with Resistencia a la tracción of 110.0 - 150.0 MPa	H22	DIN 1725-1, EN 573-3, EN 573-4	Flat

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		920.0 J/(kg·K) Show Material materials with Calor específico of 920.0 J/(kg·K)				Typical for Wrought 8000 Series Aluminium
Coeficiente de dilatación térmica	20 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683
	100 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683
Conductividad térmica	20.0 °C	210.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 210.0 - 220.0 W/(m·K)	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Temperatura de fusión		640.0 - 655.0 °C Show Material materials with Temperatura de fusión of 640.0 - 655.0 °C	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica	20.0 °C	34000000.0 - 35000000.0 S/m Show Material materials with Conductividad eléctrica of 34000000.0 - 35000000.0 S/m	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Resistividad eléctrica		2.86e-08 - 2.94e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.86e-08 - 2.94e-08 Ω·m	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Cromo	0.1 % Show Material materials with Cromo of 0.1 %	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683
Hierro	0.5 - 1.0 % Show Material materials with Hierro of 0.5 - 1.0 %	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Magnesio	0.1 % Show Material materials with Magnesio of 0.1 %	H22	EN 573-3, EN 485, EN 541, EN 546, EN 683
Manganeso	0.1 % Show Material materials with Manganeso of 0.1 %	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Silicona	0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 %	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Titanio	0.05 Show Material materials with Titanio of 0.05	H22	DIN 1725-1, EN 573-3, EN 573-4	Flat
Zinc	0.1 % Show Material materials with Zinc of 0.1 %	H22	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat